采用场发射扫描电子显微镜、广角X射线衍射、元素分析、高分辨透射电子显微镜对东丽T700S、T700G和东邦UT500 3种碳纤维的表面和断面形貌、化学组成及石墨微晶等微观组织结构进行了表征,比较了这3种碳纤维的微观结构差异,并分析了这些差异对力学性能的影响。结果表明,T700G碳元素含量较高,氮元素含量较低,它的石墨微晶尺寸较大,取向度较高,这是它比T700S拉伸模量高但断裂伸长率低的原因;UT500的表面结构与断面结构不如T700S和T700G好,微晶尺寸也较小,但它的直径略细,而且石墨微晶内(002)晶面排列比T700S和T700G更规整,导致UT500的综合力学性能略优于T700S和T700G。

Field emission scanning electron microscope, X-ray diffractometer, elemental analysis and high-reso- lution transmission electron microscope were used to characterize the surface and fracture feature, chemical composition and graphite microcrystalline structure of three kinds of carbon fibers including Toray T700S, T700G and Toho UT500. The microstructure differences of the three carbon fibers were compared and the effects of these differences in mierostructure on mechanical properties of carbon fiber were analyzed. Rustles showed that TT00G has a higher carbon content and a lower nitrogen content, larger graphite crystallite size and orientation degree, which are the reasons that it has higher tensile modulus but lower elongation at break than T700S; surface and fracture feature of UT500 were slightly worse than T700S and T700G and its graphite crys- tallite size is smaller; however, the diameter of UT500 is a little thinner and the (002) crystal faces in graphite microcrystalline arrange more ordered than TT00S and TT00G, which cause the comprehensive mechanical prop- erty of UT500 is a bit better than that of T700S and T700G

参考文献

[1] Kobets I. P;Deev I S .Carbon fibers:Structure and me chanical properties[J].Composites Science and Technolo- gy,1998,57(12):1571-1580.
[2] 贺福;赵建国;王润娥 .碳纤维工业的长足发展[J].高科技纤维与应用,2000,25(04):9-13.
[3] 罗益锋 .新世纪初世界碳纤维透视[J].高科技纤维与应用,2000,25(01):1-7.
[4] 罗益锋.炭纤维的新形势与新技术[J].新型炭材料,1995(04):13.
[5] 莆纪震;赵耀叫;陈驾英.合成纤维生产工艺学(下册)[M].北京:中国纺织出版社,1984:95.
[6] 贺福;壬茂章.碳纤维及其复台材料[M].北京:科学出版社,1995:57-59.
[7] 徐棵华;吴红枚 .PAN/DMSOf-湿法纺丝凝固工艺的研究[J].商分子材料科学勺工程,2000,16(06):163-166.
[8] 秦志全,周霞.二甲基亚砜法聚丙烯腈原丝干湿纺与湿纺成形工艺的比较[J].高科技纤维与应用,2006(03):15-18.
[9] Bunsell A R;Hearle J W S;Konopasek L et al.A pre- liminary study of the fracture morphology of acrylic fibers[J].Journal of Applied Polymer Science,1974,18:2229-2242.
[10] 张吒玺;彭洪修 .聚丙烯腈原丝结构与性能的研究[J].合成技术及应用,2000,15(03):58.
[11] 陈厚 .两种聚丙烯腈原丝结构与性能的对比研究[J].金山油化纤,2000,19(02):1-6.
[12] 王延相,何东新.聚丙烯腈纤维结构缺陷的形成和控制[J].金山油化纤,2004(04):11-16,50.
[13] 王启芬 .聚丙烯腈纤维结构及其形成过程的研究[D].山东大学,2010.
[14] 王茂章;贺福.碳纤维的制造、性质及应用[M].北京:科学出版社,1984
[15] 徐海萍,孙彦平,陈新谋.PAN基预氧化纤维表面超微结构的STM研究[J].新型炭材料,2005(04):312-316.
[16] Diefendorf R J;Tokarsky E .High-performance carbon fibers[J].Polymer Engineering and Science,1975,15(03):150-159.
[17] 贺福.碳纤维及其应用技术[M].北京:化学工业出版社,2004
[18] 殷敬华;莫志深.现代高分子物理学[M].北京:科学出版社,2001
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%