采用激光烧结(LS)+等温锻造复合工艺制各出优质粉末TC17钛合金材料,并研究了工艺过程对合金组织性能的影响.结果表明:激光烧结后的TC17合金微观组织主要由粗大β柱状晶粒组成;经相变点上、下等温锻造及热处理后,激光烧结的魏氏组织能够被有效地破碎,显微组织主要由条状和细小等轴a相组成;仅经相变点以下等温锻造及热处理后,合金组织主要由细小等轴a相组成,但由于变形不均,仍存在有少量的原始β晶粒边界.经过等温锻造、熟处理后,激光烧结合金的室温强度变化不大,但塑性大大提高,强度和塑性得到了良好地匹配.
参考文献
| [1] | Kozo Osakada;Masanori Shiomi .Flexible manufacturing of metallic products by selective laser melting of powder[J].International Journal of Machine Tools & Manufacture: Design, research and application,2006(11):1188-1193. |
| [2] | Suman Das;Marti V C Kumar .[J].Surface and Coatings Technology,2006,201:3174. |
| [3] | Srivastava D;Chang I T H;Loretto M H .[J].Intermetaiiics,2001,9:1003. |
| [4] | 张霜银;林鑫;陈静 et al.[J].稀人金属材料与工程,2007,36(10):1839. |
| [5] | 昝林;陈静;林鑫 et al.[J].稀人金属材料与工程,2007,36(04):612. |
| [6] | Roush E D;Kobryn P A;Semiatin S L .[J].Scripta Materialia,2001,45:717. |
| [7] | Semiatin S L;Kobryn P A;Roush E D .[J].Metallurgical andMaterials Transaction A,2001,32A:1801. |
| [8] | 林鑫,杨海欧,陈静,黄卫东.激光快速成形过程中316L不锈钢显微组织的演变[J].金属学报,2006(04):361-368. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%