采用溶胶凝胶法制备了Pd掺杂型铈锆固溶体粉末.XRD和XPS分析结果表明,有部分Pd进入了固溶体的晶格,主要以PdO和PdO2的形态存在;900 ℃ 50 h的老化条件并没有使Pd和Ce的价态发生明显的变化;其催化性能主要取决于氧空位的数量和活性,与Pd负载型铈锆催化剂相比,表现出较好的热稳定性能.
参考文献
| [1] | Fernández-García M;Martínez-Arias A;Iglesias-Juez A et al.Behavior of bimetallic Pd-Cr/Al2O3 and Pd-Cr/(Ce,Zr)Ox/Al2O3 catalysts for CO and NO elimination[J].Journal of Catalysis,2003,214:220. |
| [2] | Hickey N;Fornasiero P;Kaspar J et al.Effects of the nature of the reducing agent on the transient redox behavior of NM/Ce0.68Zr0.32O2 (NM=Pt,Pd,and Rh)[J].Journal of Catalysis,2001,200:181. |
| [3] | Fernández-Garc M;Martínez-Arias A;Iglesias-Juez A et al.New Pd/CexZr1-xO2/Al2O3 three-way catalysts prepared by microemulsion: Part 1.Characterization and catalytic behavior for CO oxidation[J].Applied Catalysis B:Environmental,2001,31:39. |
| [4] | Potdar HS.;Deshpande SB.;Deshpande AS.;Gokhale SP.;Date SK.;Khollam YB.;Patil AJ. .Preparation of ceria-zirconia (Ce0.75Zr0.25O2) powders by microwave-hydrothermal (MH) route[J].Materials Chemistry and Physics,2002(3):306-312. |
| [5] | Di Monte R.;Kaspar J.;Rumori P.;Gubitosa G.;Graziani M.;Fornasiero P. .Pd/Ce0.6Zr0.4O2/Al2O3 as advanced materials for three-way catalysts - Part 1. Catalyst characterisation, thermal stability and catalytic activity in the reduction of NO by CO[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2000(3/4):157-167. |
| [6] | Kenevey K;Valdivieso F;Soustelle M et al.Thermal stability of Pd or Pt loaded Ce0.68Zr0.32O2 and Ce0.50Zr0.50O2 catalyst materials under oxidising conditions[J].Applied Catalysis B:Environmental,2001,29:93. |
| [7] | Boaro M.;Dolcetti G.;Trovarelli A.;de Leitenburg C. .The dynamics of oxygen storage in ceria-zirconia model catalysts measured by CO oxidation under stationary and cycling feedstream compositions[J].Journal of Catalysis,2000(2):338-347. |
| [8] | Boaro M.;Trovarelli A.;Hwang JH.;Mason TO. .Electrical and oxygen storage/release properties of nanocrystalline ceria-zirconia solid solutions[J].Solid state ionics,2002(1/2):85-95. |
| [9] | Fornasiero P.;Kaspar J.;Montini T.;Graziani M.;Dal Santo V.;Psaro R. Recchia S. .Interaction of molecular hydrogen with three-way catalyst model of Pt/Ce0.6Zr0.4O2/Al2O3 type[J].Journal of molecular catalysis, A. Chemical,2003(0):683-691. |
| [10] | Di Monte R.;Kaspar J.;Fornasiero P.;Graziani M.;Paze C.;Gubitosa G. .NO reduction by CO over Pd/Ce0.6Zr0.4O2-Al2O3 catalysts: in situ FT-IR studies of NO and CO adsorption[J].Inorganica Chimica Acta,2002(0):318-326. |
| [11] | Basile F;Fornasari G;Gazzano M et al.Synthesis and thermal evolution of hydrotalcite-type compounds containing noble metals[J].Applied Clay Science,2000,16:185. |
| [12] | Dean J A.Lange′s Handbook of Chemistry[M].McGraw-Hill,New York,1998 |
| [13] | Datye AK.;Nelson TR.;Atanasova P.;Lyubovsky M.;Pfefferle L.;Bravo J. .Catalyst microstructure and methane oxidation reactivity during the Pd <-> PdO transformation on alumina supports[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2000(1/2):179-196. |
| [14] | Cubeiro M L;Fierro J L G .Partial oxidation of methanol over supported palladium catalysts[J].Applied Catalysis A:General,1998,168:307. |
| [15] | Hoflund GB.;Hagelin HAE.;Weaver JF.;Salaita GN. .ELS and XPS study of Pd/PdO methane oxidation catalysts[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):102-112. |
| [16] | Brun M;Berthet A;Bertolini J C .XPS,AES and Auger parameter of Pd and PdO[J].Journal of Electron Spectroscopy and Related Phenomena,1999,104:55. |
| [17] | Klingstedt F;Neyestanaki A K;Byggningsbacka R et al.Palladium based catalysts for exhaust aftertreatment of natural gas powered vehicles and biofuel combustion[J].Applied Catalysis A:General,2001,209:301. |
| [18] | Larachi F.;Pierre J.;Adnot A.;Bernis A. .Ce 3d XPS study of composite CexMn1-xO2-y wet oxidation catalysts[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2002(1/4):236-250. |
| [19] | Galtayries A.;Riga J.;Blanchard G.;Caudano R.;Sporken R. .XPS comparative study of ceria/zirconia mixed oxides: powders and thin film characterisation[J].Journal of Electron Spectroscopy and Related Phenomena,1998(0):951-956. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%