半固态金属坯料部分重熔是半固态金属触变成形工艺的重要技术环节，为了使坯料获得既细小又圆整的晶粒组织，对近液相线铸造ZK60镁合金半固态坯料进行部分重熔，通过改变重熔温度和保温时间来研究其微观组织的演化规律。结果表明：适当控制加热温度和保温时间，坯料部分重熔时可获良好的触变结构。石墨模浇注时，在600~605℃、保温10~15 min时可获得较理想的触变结构，平均晶粒尺寸达30.5μm，圆度达1.5；水冷铜模浇注时，可得出相同的结论，其晶粒平均直径为31.8μm，圆度达1.6。且坯料近液相线铸造时的冷却速率对部分重熔的进程也产生影响，适当降低铸造冷却速率，即采用石墨模能提高二次重熔组织的均匀性和稳定性。
Partial remelting is the important part of semi-solid metal (SSM) ingots forming technology. In order to obtain small and round grain organization microstructure, the microstructure evolution of ZK60 magnesium alloy SSM ingots obtained by near-liquidus casting were partially remelted, and the microstructure evolution would be investigated by controlling remelting temperature and holding time. The results indicate that good thixotropic microstructure will be obtained by controlling remelting temperature and holding time suitably. Using the graphite mould, optimizing thixotropic microstructure can be obtained at 600-605℃for 10-15 min, the average diameter of grain is 30.5μm and the roundness is 1.5. With the water-cooled copper mould, the conclusion is the same, the average grain diameter is 31.8μm and the roundness is 1.6. Meanwhile, the cooling rates during casting also affect the partial remelting progress, reducing the cooling rate properly, the graphite mould can improve the uniformity and stability of the partial remelting microstructure.
参考文献
| [1] | 刘正;张奎;曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002 |
| [2] | ZUO Tie-yong,DU Wen-bo.The developing strategy of Chinese magnesium and magnesium alloy[J].广东有色金属学报,2005(02):1-4. |
| [3] | Michiaki Yamasaki;Naoyuki Hayashi;Shogo Izumi;Yoshihito Kawamura .Corrosion behavior of rapidly solidified Mg-Zn-rare earth element alloys in NaCl solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(1):255-262. |
| [4] | C.I. Chang;X.H. Du;J.C. Huang .Achieving ultrafine grain size in Mg–Al–Zn alloy by friction stir processing[J].Scripta materialia,2007(3):209-212. |
| [5] | PENG Q M;WU Y M;FANG D Q;MENG J,WANG L M.Microstructures and properties of Mg-7Gd alloy containing Y[J]. |
| [6] | 尹忠涛;孟健;张洪杰;唐定骧 鲁化一 张文 赵贵荣 郝道德 .含铈镧混合稀土的 Mg-Al-Zn-RE 变形镁合金及其生产方法、应用[P].中国专刊:CN101824571A,2010-09-08. |
| [7] | H. Watanabe;T. Mukai;K. Ishikawa .Effect of temperature of differential speed rolling on room temperature mechanical properties and texture in an AZ31 magnesium alloy[J].Journal of Materials Processing Technology,2007(26):644-647. |
| [8] | M.R. Barnett;Z. Keshavarz;A.G. Beer .Non-Schmid behaviour during secondary twinning in a polycrystalline magnesium alloy[J].Acta materialia,2008(1):5-15. |
| [9] | 陈振华,夏伟军,程永奇,傅定发.镁合金织构与各向异性[J].中国有色金属学报,2005(01):1-11. |
| [10] | CIZEK P;BARNETT M R .Characteristics of the contraction twins formed chose to the fracture suiace in Mg-3Al-1Zn alloy deformed in tension[J].Scripta Materialia,2008,59(09):959-962. |
| [11] | 毛卫民.半固态金属成形技术[M].北京:机械工业出版社,2004:15-128. |
| [12] | 乐启炽,张新建,崔建忠,路贵民,欧鹏.AZ91D镁合金近液相线铸造半固态坯料的部分重熔[J].金属学报,2002(12):1266-1272. |
| [13] | 黎文献.镁及镁合金[M].长沙:中南大学出版社,2005 |
| [14] | 乐启炽,欧鹏,吴跃东,路贵民,崔建忠,邱竹贤.AZ91D镁合金近液相线铸造研究[J].金属学报,2002(02):219-224. |
| [15] | WANG Kai,LIU Changming,HAN Zhaotang,CAO Jianyong,ZHANG Zonghe.Research on semi-solid thixoforming process of AZ91D magnesium alloy brackets for generators in JH70-type motorbikes[J].稀有金属（英文版）,2005(04):381-391. |
| [16] | Frank Czerwinski .Fundamentals of Semisolid Magnesium Molding[J].JOM,2008(11):82-86. |
| [17] | Le Qichi,Wang Zhongjun,Cui Jianzhong,Xu Baoqin.Partial Remelting of Thixotropic Magnesium-Rare Earth Alloy from Near Non- Equilibrium- Liquidus Casting[J].稀土学报（英文版）,2005(06):737-741. |
| [18] | 乐启炽,崔建忠,路贵民,欧鹏.两相区铸造AZ91D半固态坯料的部分重熔工艺与组织演变[J].中国有色金属学报,2003(06):1488-1493. |
| [19] | ZENIT R;HUNT M L;BRENNEN C E .On the direct and radiated components of the collisional particle pressure in liquid-solid flows[J].Applied Scientific Research,1998,58(1/4):305-317. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%