Samples with ultrafine grained austenite were prepared by repetitive rapid heating and quenching for three times and were used to investigate the dynamic microstructural evolving behaviors at different temperatures. A simultaneous development of dynamic straininduced transformation (DSIT) and austenite grain growth was detected at the deformation temperatures above Ar3, while only DSIT happened as the deformation proceeded at lower temperatures close to and below Ar3. In addition, a reverse ferritetoaustenite transformation was also observed. Most of the straininduced ferrite nucleated on the boundaries of ultrafine prior austenite grains, especially at the corners and no evidence about intragranular nucleus was obviously obtained.