通过高温电阻炉对含碳球团还原熔分的行为进行热态模拟研究,考察温度、配碳比、化学成分等因素对球团还原熔分的影响程度.结果表明,温度、配碳比和球团传热方向上的尺寸是控制球团还原熔分的关键;化学成分对还原速率影响不明显,但是通过改变渣的组成可对渣铁熔分起促进或抑制作用.
参考文献
[1] | 潘毓淳;黄务涤;万天骥 .转底炉生产珠铁及分离方法[P].CN 1186863,1998-07-08. |
[2] | 万天骥;任大宁;孔令坛 .煤基热风转底炉熔融炼铁法[P].CN 1443856A,2003-09-24. |
[3] | 晓苏 .Itmk3--第三代煤基直接还原炼铁技术[J].钢铁,2002,37(06):40-43. |
[4] | Lehtinen Larry .Method and Apparatus for Producing Molten Iron From Iron Oxides[P].WO 9951783,1999-04-17. |
[5] | Osamu Tsuge;Shoichi Kikuchi;Koji Tokuda.Successful Iron Nuggets Production at Itmk3 Pilot Plant[A].Warrendale:Iron and Steel Society/AIME,2002:511-517. |
[6] | Lehtinen Larry;Steven D Rutherford.Messabi Nugget Project:New Ironmaking Technology of the Future[A].Warrendale:Iron and Steel Society/AIME,2003:1043-1048. |
[7] | Fruehan R J .New Steelmaking Process:Drivers,Requirements,Potential Impact[J].Ironmaking and Steelmaking,2005,32(01):3-8. |
[8] | Kazuhiro NAGATA;Rie KOJIMA;Taichi MURAKAMI .Mechanisms of Pig-iron Making from Magnetite Ore Pellets Containing Coal at Low Temperature[J].ISIJ International,2001(11):1316-1323. |
[9] | Yoshitaka SAWA;Tetsuya YAMAMOTO;Kanji TAKEDA .New coal-based process to produce high quality DRI for the EAF[J].ISIJ International,2001(Suppl.):17-21. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%