研究了用应变诱发熔化激活法(SIMA)制备的半固态Al-4Cu-Mg合金在不同变形温度、变形程度和应变速率下半固态压缩变形时的微观组织演变.研究结果表明:在半固态条件下,随变形温度的升高,晶粒平均尺寸增大,分形维数减小;变形程度增大,晶粒平均尺寸减小,分形维数先减小后增大;应变速率增大,晶粒平均尺寸先减小后略有增大,且在小的应变速率下,晶粒平均尺寸随应变速率变化的趋势较大,分形维数随着应变速率的增大而增大.
参考文献
[1] | Flemings M C .Behaviour of Metal Alloys in the Semisolid State[J].Metallurgical and Materials Transactions,1991,22A:957-981. |
[2] | 王平,路贵民,崔建忠.液相线半连续铸造A356铝合金触变成形的组织与性能[J].稀有金属材料与工程,2002(05):382-384. |
[3] | KANG C G;Yoon J H;Seo Y H .The Upsetting Behavior of Semisolid Aluminum Material Fabricated by a Mechanical Stirring Process[J].Journal of Materials Processing Technology,1997,66:30-38. |
[4] | Jae Chan Choi;Hyung Jin Park .Microstructural characteristics of aluminum 2024 by cold working in the SIMA process[J].Journal of Materials Processing Technology,1998(1/3):107-116. |
[5] | 江海涛;卢雅琳;黄维超;李淼泉 .Microstructure Evolution and Mechanical Properties of the Semisolid Al-4Cu-Mg Alloy[J].Materials Characterization,2003,51:1-10. |
[6] | 江海涛,黄维超,卢雅琳,李淼泉.半固态LY11铝合金的组织演变研究[J].稀有金属材料与工程,2004(08):869-872. |
[7] | 郭均;丁志勇;谢水生 et al.Deformation Behavior of Semisolid Al-6.6%Si Alloy[J].中国有色金属学报,2000,10(z1):115-119. |
[8] | Hardy S C;Voorhees P W .Ostwald Ripending in a System with High Volume Fraction of Coarsening Phase[J].Metallurgical and Materials Transactions,1988,19A:2713-2721. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%