采用化学改性法对芳纶纤维进行表面处理,研究了改性前后芳纶纤维对水泥基复合材料强度及抗冲击性能的影响.结果表明:芳纶纤维的掺入可以提高水泥砂浆的抗折强度和抗冲击性能,经化学改性后的芳纶纤维增强效果更加明显.当掺杂纤维的体积分数为1.0%时,化学改性前后芳纶纤维增强水泥砂浆试样与基准砂浆试样相比,其28天抗折强度分别提高了15.18%和23.85%,抗冲击韧性分别提高了276.74%和294.54%.采用SEM对芳纶纤维表面微观形貌及试样断口形貌进行了观察,利用XPS对改性前后芳纶纤维表面元素变化进行了研究,探讨了芳纶纤维对水泥砂浆的增强机制.
参考文献
| [1] | 张礼和,谈慕华,马一平,等.PP纤维水泥界面粘接与抗干缩开裂性能研究[J].建筑材料学报,2001,18(1):17-21.Zhang Lihe,Tan Muhua,Ma Yiping,et al.Study on interface bonding of PP fiber-cement and antishringkage performance[J].Journal of Building Materials,2001,18(1):17-21. |
| [2] | Wan Y Z,Wang Y L,He F,et al.Mechanical performance of hybrid bismaleimide composites reinforced with threedimensional braided carbon and Kevlar fabrics[J].Composites,2007,38(2):495-504. |
| [3] | Nelson P K,Li V C,Kamada T.Fracture toughness of microfiber reinforced cement composites[J].Journal of Materials in Civil Engineering,2002,14(5):384-391. |
| [4] | 刘丽芳,王培铭,杨晓杰.聚丙烯纤维参数对水泥砂浆抗干缩开裂性的影响[J].建筑材料学报,2005,8(3):239-243.Liu Lifang,Wang Peiming,Yang Xiaojie.Effects of characteristics of polypropylene fiber on anti-dry-shrinkage cracking property of cement mortar[J].Journal of Materials in Civil Engineering,2005,8(3):239-243. |
| [5] | 王杨,李鹏,于运花,等.芳纶纤维的磷酸表面处理及其树脂基复合材料界面性能[J].复合材料学报,2007,24(3):7-12.Wang Yang,Li Peng,Yu Yunhua,et al.Interfacial properties of phosphorous acid modified Kevlar fiber reinforced epoxy resin composites[J].Acta Materiae Compositae Sinica,2007,24(3):7-12. |
| [6] | 周正刚,李敏,蒋诗才.Kevlar织物NHs等离子体表面改性研究[J].航空材料学报,2009,29(3):83-87.Zhou Zhenggang,Li Min,Jiang Shicai.Study on NH3 plasma surface modification of Kevlar fabric[J].Journal of Aeronautical Materials,2009,29(3):83-87. |
| [7] | 熊佳,黄英,王琦洁.高性能纤维的发展和应用[J].玻璃钢/复合材料,2004(5):49-52.Xiong Jia,Huang Ying,Wang Qijie.Development and application of high performance fiber[J].Fiber Reinforced Plastics/Composite,2004(5):49-52. |
| [8] | 袁海根,曾金芳,杨杰,熊艳丽.芳纶表面改性研究进展[J].高科技纤维与应用,2005,30(2):26-33.Yuan Haigen,Zeng Jinfang,Yang Jie,Xiong Yanli.The review of surface modification of aramid fibers[J].Hi-tech Fiber & Application,2005,30(2):26-33. |
| [9] | 路向辉,王吉贵.芳纶纤维表面处理技术的发展概况[J].塑料工业,2007,35(S1):84-86.Lu Xianghui,Wang Jigui.General situation of development of surface treatment technology for aramid fiber[J].China Plastics Industry,2007,35(S1):84-86. |
| [10] | 袁海根,王汝敏,艾涛.表面处理对Kevlar纤维复合材料界面结合强度的影响[J].化学推进剂与高分子材料,2005,3(5):38-41.Yuan Haigen,Wang Rumin,Ai Tao.Effect of fiber surface treatment on interface binding strength of Kevlar composites[J].Chemical Propellants & Polymeric Materials,2005,3(5):38-41. |
| [11] | 龚益,徐至钧.纤维混凝土与纤维砂浆施工应用指南[M].北京:中国建材工业出版社,2005;69-72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%