研究将普通挤压和等通道角挤压工艺结合而开发出的新型复合挤压工艺。采用有限元技术建立具有不同摩擦系数和不同转角的模型,模拟镁合金复合挤压过程,分析复合挤压力变化特征,以及挤压过程的应变累积情况。结果表明,摩擦系数增大或者通道角减小,复合挤压的挤压力和等效应变增加。摩擦和转角均会引起变形的不均匀性,摩擦因数越大,通道转角越小,其不均匀性越大。在摩擦因数为0.3,通道转角为120°时可以获得较大且均匀的等效应变。
参考文献
| [1] | Li B;Joshi S;Azevedo K et al.Dynamic testing at high strain rates of and Engineering A[J].,2009,517(1-2):24-29. |
| [2] | Su C W;Lu L;Lai M O .A model for the grain refinement mechanism[J].Materials Science and Engineering A,2006,434(1-2):227-236. |
| [3] | Wang Q D;Chen Y J;Lin J B et al.Microstructure and properties of magnesium alloy processed by a new severe plastic deformation method[J].M aterials Letters,2007,61(23-24):4599-4602. |
| [4] | A. V. Nagasekhar;Yip Tick-Hon .Optimal tool angles for equal channel angular extrusion of strain hardening materials by finite element analysis[J].Computational Materials Science,2004(3/4):489-495. |
| [5] | S.M. Masoudpanah;R. Mahmudi .The microstructure, tensile, and shear deformation behavior of an AZ31 magnesium alloy after extrusion and equal channel angular pressing[J].Materials & design,2010(7):p.3512. |
| [6] | ZHANG Jing,ZHANG Ke-shi,WU Hwai-Chung,YU Meihua.Experimental and numerical investigation on pure aluminum by ECAP[J].中国有色金属学报（英文版）,2009(05):1303-1311. |
| [7] | 张丁非,张钧萍,胡红军,李鹏程.模具结构对镁合金棒材裂纹形成的有限元和实验研究[J].材料热处理学报,2011(02):151-156. |
| [8] | Seung Chae Yoon;Min Hong Seo;A. Krishnaiah .Finite element analysis of rotary-die equal channel angular pressing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):289-292. |
| [9] | Xu Shu-bo;Zhao Guo-qun;Ren Xu-fang et al.Numerical investigation of aluminum deformation behavior in three-dimensional continuous confined strio shearing process[J].Materials Science and Engineering A,2008,476(1-2):281-289. |
| [10] | Jin, YG;Son, IH;Kang, SH;Im, YT .Three-dimensional finite element analysis of multi-pass equal-channel angular extrusion of aluminum AA1050 with split dies[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):152-155. |
| [11] | Zenji Horita;Kiyoshi Matsubara;Koichi Makii;Terence G. Langdon .A two-step processing route for achieving a superplastic forming capability in dilute magnesium alloys[J].Scripta materialia,2002(4):255-260. |
| [12] | K. Matsubara;Y. Miyahara;Z. Horita .Developing superplasticity in a magnesium alloy through a combination of extrusion and ECAP[J].Acta materialia,2003(11):3073-3084. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%