在27SiMn基体上制备一种新型的Ni-P-Ti3AlC2化学复合镀层,利用SEM,XRD对镀层形貌和物相进行表征,利用显微硬度计和磨粒磨损实验机分别对复合镀层的硬度和耐磨性进行研究.结果表明:Ni-P-Ti3AlC2复合镀层的沉积方式为颗粒堆积,相对于Ni-P二元镀层表面比较粗糙;复合镀层为非晶态结构,其硬度和耐磨性比二元镀层显著提高.
A novel Ni?P?Ti3AlC2 electroless composite plating was prepared on 27SiMn alloy. The surface morphology and phase analysis of the plating were characterized with SEM and XRD,meanwhile,the hardness and wear resistance of the plating were analyzed by microhardness tester and abrasive wear machine,respectively. The results show that the depositional style of Ni?P?Ti3AlC2 plating is the particle packing,and the surface of composite plating becames more coarser compared to that of electroless Ni?P plating;the XRD results reveal that the composite deposits have a typical amorphous structure. The microhardness and wear resistance of the composite plating are superior to that of Ni?P plating.
参考文献
[1] | Bender D;Chhouk B;Fong R.Explosively formed penetrators(EFP) with canted fins[A].Switzerland:Interlaken,2001 |
[2] | 门建兵,蒋建伟,万丽珍.带尾翼EFP形成的三维数值模拟研究[J].北京理工大学学报,2002(02):166-168. |
[3] | 宋顺成,高平,才鸿年.贫铀合金材料自锻弹丸的数值模拟[J].应用数学和力学,2003(09):951-955. |
[4] | Jun Wu;Jingbo Liu;Yixin Du .Experimental and numerical study on the flight and penetration properties of explosively-formed projectile[J].International journal of impact engineering,2007(7):1147-1162. |
[5] | 常向阳,王自力.爆炸成型弹丸侵彻钢靶的ALE算法[J].解放军理工大学学报(自然科学版),2004(03):70-73. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%