研究了 IN718高温合金在650℃下的熔盐(75%Na2SO4+25%NaCl)热腐蚀行为及其对合金力学性能的影响.研究表明,IN718合金热腐蚀层分为两层,外层由Fe3O4,FeCr2O4和Cr2O3等氧化物组成,内层由Ni和Ni的硫化物组成.热腐蚀过程中S沿晶界快速扩散并在晶界形成硫化物.IN718合金在650℃,100 h浸盐热腐蚀预处理后,室温拉伸性能和650℃拉伸强度变化不大,合金在650℃拉伸塑性略微降低,但650℃,700 MPa持久性能显著降低,其主要原因是S降低晶界强度,同时外加应力提高腐蚀速率.
参考文献
[1] | Greeene G A;Finfrock C C .[J].Oxidation of Metals,2001,55:505. |
[2] | Paton N E;Robertson W M;Mansfeld F .[J].Metallurgical and Materials Transactions,1973,4:317. |
[3] | John F;Radavich .[J].Journal of Metals,1988,7:35. |
[4] | Loria E A .[J].Journal of Metals,1988,7:36. |
[5] | Zhu Rizhang;Guo Manjiou;Zuo Yu .[J].Oxidation of Metals,1987,27:253. |
[6] | Gaskell D R.Introduction to Metallurgical Thermodynamics,2nd ed[M].New York:McGraw-Hill,1981 |
[7] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:385. |
[8] | Li Jian;Yun C Y;Farooque M .[J].Corrosion Science,2000,42:1573. |
[9] | Guo Jianting;Ranucci D;Picco E.[A].Warrendale,PA:TMS-AIME,1984:689. |
[10] | Sadananda K;Shahinian P .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1977,8:439. |
[11] | Yah Xu;John L .[J].Materials Science and Engineering,1999,260:48. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%