利用选区激光熔化(SLM)工艺制备了纳米TiC固溶增强W基复合材料,研究了不同激光线能量密度(η)对SLM成形试件致密度、微观组织、显微硬度和摩擦磨损性能的影响.结果表明:当η过低时,成形试件中存在明显残余孔隙;而当η过高时,因热应力影响,成形试件中形成显微裂纹,均降低成形致密度.而在适宜的n=2.1 kJ/m时,SLM成形试件致密度达到理论密度的94.7％,平均显微硬度(HV0.2)高达8062 MPa;摩擦磨损实验结果表明试件的摩擦系数曲线平稳,平均摩擦系数值为0.583,相应的磨损率较低为0.69× 10-15 m3/N·m;激光成形试件中形成均匀分布的柱状晶,平均晶粒直径为0.73 μm.
参考文献
| [1] | Fahim NF .Thermal conductivity of plasma-sprayed W/SiC composite for high-temperature energy applications[J].Surface & Coatings Technology,2008(9):1696-1703. |
| [2] | Kurishita H;Amano Y;Kobayashi S;Nakai K;Arakawa H;Hiraoka Y;Takida T;Takebe K;Matsui H .Development of ultra-fine grained W-TiC and their mechanical properties for fusion applications[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2007(b):1453-1457. |
| [3] | 郭双全,葛昌纯,冯云彪,周张健,周海滨,王纯.面向等离子体材料钨厚涂层的制备及表征[J].稀有金属材料与工程,2011(12):2167-2170. |
| [4] | Kurishita, H;Matsuo, S;Arakawa, H;Sakamoto, T;Kobayashi, S;Nakai, K;Takida, T;Kato, M;Kawai, M;Yoshida, N .Development of re-crystallized W-1.1%TiC with enhanced room-temperature ductility and radiation performance[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2010(1/3):87-92. |
| [5] | 种法力,于福文,陈俊凌.W-TiC合金面对等离子体材料及其电子束热负荷实验研究[J].稀有金属材料与工程,2010(04):750-752. |
| [6] | Zheng, L.;Schmitz, G.;Meng, Y.;Chellali, R.;Schlesiger, R. .Mechanism of intermediate temperature embrittlement of ni and ni-based superalloys (Review)[J].Critical Reviews in Solid State and Materials Sciences,2012(3):181-214. |
| [7] | 郑欣,白润,王东辉,蔡晓梅,王峰,夏明星,喻吉良.航天航空用难熔金属材料的研究进展[J].稀有金属材料与工程,2011(10):1871-1875. |
| [8] | Battabyal, M.;Sch?ublin, R.;Sp?tig, P.;Baluc, N..W-2wt.%Y _2O _3 composite: Microstructure and mechanical properties[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:53-57. |
| [9] | 欧阳明亮,秦明礼,曲选辉,罗铁钢.加镍钨粉的活化烧结研究进展[J].稀有金属材料与工程,2009(z1):122-125. |
| [10] | 杨永强,王迪,吴伟辉.金属零件选区激光熔化直接成型技术研究进展[J].中国激光,2011(06):54-64. |
| [11] | 黄卫东,林鑫.激光立体成形高性能金属零件研究进展[J].中国材料进展,2010(06):12-27. |
| [12] | 王华明.金属材料激光表面改性与高性能金属零件激光快速成形技术研究进展[J].航空学报,2002(05):473-478. |
| [13] | 张铁邦,胡锐,钟宏,葛光男,李金山.激光区熔定向凝固Gd5Si4合金的显微组织特征[J].稀有金属材料与工程,2012(10):1837-1841. |
| [14] | 陈静,赵晓明,杨海欧,冯莉萍,林鑫,黄卫东.激光快速成形粉末高温合金的力学性能研究[J].稀有金属材料与工程,2008(09):1664-1668. |
| [15] | 韩勇,范景莲,刘涛,成会朝,田家敏.高密度纯钨的低温活化烧结工艺及其致密化行为[J].稀有金属材料与工程,2012(07):1273-1278. |
| [16] | 张苹苹,沈卫平,周亚南,马明亮,张庆玲,王青云.纳米碳化钽对SPS烧结钨显微结构的影响[J].稀有金属材料与工程,2012(08):1431-1434. |
| [17] | 肖志霞,郑立静,杨莉莉,闫洁,张虎.温度梯度对定向凝固TiAl基合金片层取向的影响[J].金属学报,2010(10):1223-1229. |
| [18] | 刘文胜,张佳佳,马运柱,赵亚旭,徐志刚,黄伯云.微波烧结工艺对钨基合金挤压棒坯显微组织及力学性能的影响[J].稀有金属材料与工程,2012(07):1284-1288. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%