以三羟甲基丙烷为核、二羟甲基丙酸为单体,分别采用"一步法"和"准一步法"合成了1～5代脂肪族超支化聚酯(HBPE).以硬脂酸对聚酯进行了端基改性,并对两类改性后的HBPE与线型聚丙烯(PP)共混物的流变性和力学性能进行了比较.结果表明,3%HBPE的加入即可大幅度降低PP熔体的黏度,而准一步法比一步法合成的聚酯具有更好的改性效果.与纯PP相比,当共混物中准一步4代(pg4)政性聚酯的添加量为3%,拉伸强度几乎相同,但降低熔体黏度50%以上,伸长率提高14%.
参考文献
| [1] | MACKAY M E;HENSON D J .[J].Journal of Rheology,1999,43(03):781-793. |
| [2] | Schmaljohann D.;Haessler R.;Voit B.I.;Froehling P.E.;Mostert B.;Loontjens J.A.;Poetschke P. .Blends of amphiphilic, hyperbranched polyesters and different polyolefins[J].Macromolecules,1999(19):6333-6339. |
| [3] | MULKEPN T J;BECK T N C .[J].Polymer,2000,41(09) |
| [4] | Nunez CM.;Andrady AL.;Khan SA.;Chiou BS. .Solution rheology of hyperbranched polyesters and their blends with linear polymers[J].Macromolecules,2000(5):1720-1726. |
| [5] | 谭惠民;罗运军.超支化聚合物[M].北京:化学工业出版社,2005 |
| [6] | Malmstrom E.;Hult A. .KINETICS OF FORMATION OF HYPERBRANCHED POLYESTERS BASED ON 2,2-BIS(METHYLOL)PROPIONIC ACID[J].Macromolecules,1996(4):1222-1228. |
| [7] | BURKINSHOW S M;FROEHLING P E;MIGNANELLI M .[J].Dyes and Pigments,2002,53:229-235. |
| [8] | 赵宝辉,巴信武,侯文龙,王素娟,韩颖慧.超支化聚（酰胺-酯）/聚氯乙烯共混体系流变性能及其力学性能研究[J].高分子材料科学与工程,2003(02):157-160. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%