采用真空蒸镀方法在镀锌钢板表面沉积一定厚度的镁,然后对其进行合金化退火处理获得了新型锌镁合金镀层.通过扫描电子显微镜(SEM)观察了镀层表面及截面、切边的微观组织,利用能谱(EDS)进行了微区成分分析;应用盐雾试验,电化学方法对锌镁镀层钢板的耐蚀性进行了研究,利用X射线衍射分析了镀层及镀层盐雾试验腐蚀产物的物相组成.结果表明,蒸镀锌镁镀层主要由MgZn2及其他锌镁合金相组成,锌镁镀层比普通镀锌板具有更强的耐腐蚀性能,同时有更好的切边耐腐蚀性能.在宏观上表现为蒸镀锌镁镀层腐蚀产物相对于纯锌镀层更加致密,在电化学行为上表现为蒸镀锌镁镀层具有更小的腐蚀电流密度和更高的极化电阻.
参考文献
| [1] | NAKAKOJI H;NAKAJIMA S;YASUDA A et al.Method of producing a steel sheet plated with zincmagnesium alloy superior both in plating adhesion and corrosion resistance and sheets plated with it[P].USA,19910570554,1991-05-22. |
| [2] | Kazumi NISHIMURA;Hidetoshi SHINDO;Hiromasa NOMURA .Corrosion Resistance of Hot Dip Zn-Mg Galvanized Steel Sheet[J].鉄と鋼,2003(1):174-179. |
| [3] | KAWAFUKU J;KATOH J;TOYAMA M et al.Properties of zinc alloy coated steel sheets obtained by continuous vapor deposition pilot-line[J].Training,1991,2011:11-04. |
| [4] | Schuhmacher B.;Schwerdt C.;Seyfert U.;Zimmer O. .Innovative steel strip coatings by means of PVD in a continuous pilot line: process technology and coating development[J].Surface & Coatings Technology,2003(0):703-709. |
| [5] | Christian Schwerdt;Monika Riemer;Stefan Kohler;Bernd Schuhmacher;Michael Steinhorst;Axel Zwick .Application related properties of novel ZE-Mg coated steel sheet[J].Stahl und Eisen,2004(9):69-74. |
| [6] | KOLL T;ULLRICH K;FADERL J et al.Properties and potential applications of novel ZnMg alloy coatings on steel sheet[J].Revue de Métallurgie,2004,101(7/8):543-550. |
| [7] | MICHEL B.阿赛洛公司汽车用钢新品种简介[J].钢铁译文集,2007(1):18. |
| [8] | Masao MORISHITA;Koichiro KOYAMA;Momonori MURASE;Yoshitaka MORI .Improvement in the Corrosion Resistance of Zinc-plated Steel by Electrodeposition of Magnesium from a Molten Salt[J].ISIJ International,1996(6):714-719. |
| [9] | M.Morishita .Inhibition of Anodic Dissolution of Zinc-plated Steel by Electro deposition of Magnesium from a Molten Salt[J].ISIJ International,1997(1):55-58. |
| [10] | 薛雷刚,吕春雷,印仁和,郁祖湛,王卫江,杨立红.镀锌钢板蒸镀镁层的耐腐蚀机理[J].材料保护,2010(04):87-89,94. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%