通过对不同有机硅耐高温树脂以及表面抗污助剂的筛选,研制了一种单组分、低表面能的耐沾污涂层,确定了较佳的工艺条件:C型氟改性有机硅树脂100 g,表面抗污剂KW3 1.5 g,230℃固化20 min.与市售产品进行比较,对此条件下制备的涂层进行了耐高温和人工加速老化试验,测试了涂层的综合性能.结果表明,所制备的涂层外观平整、光滑,附着力1级,铅笔硬度6H,冲击强度50 kg-cm,水接触角106°,油珠流动时间26 s,经过人工加速老化800 h以及在300℃下加热72 h后,涂层仍具有良好的疏油、疏水特性.
参考文献
| [1] | 黄月文.几种低表面能含硅（氟）涂料的性能[J].化学与黏合,2006(03):194-197. |
| [2] | 张振,何国.聚氨酯耐沾污性涂料的研制[J].涂料技术与文摘,2011(11):35-37. |
| [3] | 潘文亮.耐沾污木器漆的研制[J].上海涂料,2010(02):5-6. |
| [4] | 雷辉,卢鹉,郭家胜,曾一兵,李颖.疏水涂层的制备及性能[J].宇航材料工艺,2011(05):63-65. |
| [5] | Notsu H;Kubo W;Shitanda I;Tatsuma T .Super-hydrophobic/super-hydrophilic patterning of gold surfaces by photocatalytic lithography[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2005(15):1523-1527. |
| [6] | Luo ZZ;Zhang ZZ;Hu LT;Liu WM;Guo ZG;Zhang HJ;Wang WJ .Stable bionic superhydrophobic coating surface fabricated by a conventional curing process[J].Advanced Materials,2008(5):970-974. |
| [7] | 超疏油表面研究获进展[J].石油化工应用,2012(04):112-112. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%