采用等温凝固淬火工艺与差热扫描量热相结合的方法对高Cr铸造镍基高温合金K4648的凝周过程进行研究,得到合金在不同温度下的等温凝固组织、相析出顺序图和凝固特性曲线.结果表明:K4648合金的液相线温度为1340℃,由DSC确定的宏观同相线(3.1%残余液相,体积分数,下同)和等温凝固泫确定的微观固相线(0.5%残余液相)温度分别为1248和1180℃.K4648合金固、液相线温度范围内的初生相主要为MC碳化物和α-Cr相,它们的析出温度分别为1310和1190℃.初生α-Cr相同溶30%(原子分数)以上的Ni,显微硬度是基体的3倍,是一种脆性相.凝固过程中Cr的严重枝晶间偏析促进了该相的形成,初生α-Cr相在铸造过程中应加以控制.
参考文献
| [1] | Radavich J F.Superalloys 718,625 and Various Derivatives[M].Pennsylvania:TMS,1997:409. |
| [2] | Fernade Z R;Lecomte J C;Kattamis T Z .[J].Metallurgical and Materials Transactions,1978,9A(10):1381. |
| [3] | 郑运荣 .[J].金属学报,1986,22(02):A119. |
| [4] | Zhu Yaoxiao;Zhang Shunnan;Xu Leying.Superalloys 1988[M].Pennsylvania:TMS,1988:703. |
| [5] | WANG Xiao-ping,ZHENG Yun-rong,XIAO Cheng-bo,WANG Bei-lei.Isothermal solidification behavior of typical Ni3Al base superalloy IC6[J].中国有色金属学会会刊,2000(04):430. |
| [6] | Zheng Liang;Gu Chenqing;Zheng Yunrong .[J].Scripta Materialia,2004,50:435. |
| [7] | Hobbs R A;Tin S;Rae C M F.Superalloys 2004[M].Pennsylvania:TMS,2004:819. |
| [8] | 严晓峰;马惠萍;卢亚轩 et al.[J].材料工程,2002,3:28. |
| [9] | 董建新,张麦仓,曾燕屏.新型Ni-Cr基GH648合金成分对热力学平衡相析出行为的影响[J].稀有金属材料与工程,2005(01):51-55. |
| [10] | 董建新,谢锡善.不同Cr含量高温合金中α-Cr相析出行为及作用[J].金属学报,2005(11):1159-1166. |
| [11] | 郑亮,谷臣清,张国庆.Ta对低Cr高W铸造镍基高温合金显微组织的影响[J].稀有金属材料与工程,2005(02):194-198. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%