通过融熔缩聚法合成出一种低成本的不饱和聚酯酰胺脲树脂并表征了其性能.以此为基体,聚磷酸钙纤维(CPPF)为增强体,引入一定量的交联剂和引发-促进剂经室温交联后再在一定温度深度交联成可完全降解的CPPF/不饱和聚酯酰胺脲树脂复合材料,研究了其物理力学和降解性能.结果表明,合成的基体树脂中加入20％交联剂室温预交联再热处理后复合材料具有较高的力学强度;当CPPF的质量分数超过60％时,复合材料的力学强度出现下降的趋势,降解3个月后,含30％CPPF和50％CPPF的复合材料的弯曲强度分别能保持143MPa和148MPa.
参考文献
| [1] | Ong JL.;Chan DCN. .Hydroxyapatite and their use as coatings in dental implants: A review [Review][J].Critical Reviews in Biomedical Engineering,2000(5/6):667A-707A. |
| [2] | Sullivan J;Uden M;Robinson KP;Sooriakumaran S .Rehabilitation of the trans-femoral amputee with an osseointegrated prosthesis: the United Kingdom experience.[J].Prosthetics and orthotics international,2003(2):114-120. |
| [3] | Li LH;Kong YM;Kim HW;Kim YW;Kim HE;Heo SJ;Koak JY .Improved biological performance of Ti implants due to surface modification by micro-arc oxidation.[J].Biomaterials,2004(14):2867-2875. |
| [4] | 贺倩,郭文迅,彭荡,何姣.淀粉基可降解高吸水性功能膜的制备及性能[J].石油化工,2011(06):655-660. |
| [5] | 方敏,郭文迅,孙翔月,孙晓.改性不饱和聚酯酰胺脲紫外光固化涂料的性能研究[J].化工新型材料,2009(06):69-71,99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%