采用电弧喷涂技术在Q235钢基体上制备出纯锌、Zn-A1合金和zmAl伪合金涂层。通过浸泡试验和电化学测试考察涂层在3．5％NaCl溶液中的腐蚀行为，并结合扫描电镜（SEM）和X射线衍射仪（XRD）分析了涂层腐蚀后的表面形貌及腐蚀产物的相结构。结果表明，在3．5％NaCl溶液中三种涂层的耐腐蚀性按Zn_Al伪合金涂层、ZnA1合金涂层、Zn涂层的顺序依次降低。
Pure Zn, Zn-A1 alloy and Zn-A1 pseudo-alloy coatings were prepared on Q235 steel surface by arc spraying technique. The corrosion resistance of these coatings was investigated by immersion testing and electrochemical measurements in 3.5%NaC1 solution. The surface morphology of the samples after test and the phase composition o{ corrosion products were analyzed by using electron microscopy （SEM） and X-ray diffraction （XRD）. The results show that the corrosion resistance of the coatings decreased sequentially in the order of Zn-AI pseudo alloy coating, Zn-A1 alloy coating, and pure Zn coating.
参考文献
| [1] | R.M. Souto;L. Fernandez-Merida;S. Gonzalez;D.J. Scantlebury .Comparative EIS study of different Zn-based intermediate metallic layers in coil-coated steels[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(5):1182-1192. |
| [2] | 付东兴,徐滨士,李庆芬,张伟,魏世丞,陈永雄,白金元.高速电弧喷涂技术在防腐工程领域的研究现状[J].材料导报,2007(03):94-96,100. |
| [3] | 李言涛,侯保荣.海洋环境下热喷涂锌、铝及其合金涂层防腐蚀机理研究概况[J].材料保护,2005(09):30-34. |
| [4] | 徐滨士,马世宁,刘世参,朱胜,王海斗.绿色再制造工程在军用装备中的应用[J].空军工程大学学报(自然科学版),2004(01):1-5. |
| [5] | 孔爱民.热喷铝防腐技术在海洋平台防腐中的应用研究[J].全面腐蚀控制,2008(04):32-34. |
| [6] | 王德奎,沈承金,贾志永.钢桥面沥青混凝土铺装层下热喷锌涂层的腐蚀行为[J].腐蚀与防护,2007(09):445-448. |
| [7] | 袁涛,贺定勇,蒋建敏.钢结构热喷涂长效防腐蚀技术的研究与发展[J].腐蚀与防护,2008(04):207-210. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%