以Mo粉、Fe-B合金粉、Fe粉、Al粉为基本原料,磷酸二氢铝为粘结剂制备成型料浆,采用刷涂法在Q235钢基体上形成涂层,在真空烧结炉中通过固相反应法于860℃制备了三元硼化物陶瓷涂层.采用X射线衍射仪(XRD)、扫描电镜(SEM)、差示扫描量热仪(DSC)研究了粉体和涂层的物相组成、表面形貌和反应机理,并对涂层的结合强度、耐磨性和耐蚀性进行了测试.结果表明,球磨过程中有少量Mo2FeB2、A1Fe3 生成,860℃固化后Mo2FeB2、Mo2FeB4 等新相生成;涂层和基体形成了良好的冶金结合,结合强度可达14.15MPa;涂层具有比钢基体更优异的耐磨性和耐蚀性,封孔后性能更佳.
参考文献
| [1] | 黄巍岭 .金属陶瓷硬质覆层材料的应用基础研究[D].山东大学,2008. |
| [2] | 马壮,魏宝佳,李智超.金属表面热化学反应法陶瓷涂层研究现状及工艺名称商榷[J].硅酸盐通报,2007(05):990-993. |
| [3] | Ken-ichi Takagi .High tough boride base cermets produced by reaction sintering[J].Materials Chemistry and Physics,2001,67:214. |
| [4] | Yu Haizhou;Zheng Yong;Liu Wenjun et al.Effrct of V content on the microstructure and mechanical properties of Mo2 FeB2 based cermets[J].Materials & Design,2010,31:2680. |
| [5] | Nishiyama K;Keino M;Furuyama Y et al.Internal fric-tion of boride cermets at elevated temperatures[J].Journal of Alloys and Compounds,2003,355:97. |
| [6] | Ken-ichi Takagi .Development and application of high str-ength ternary boride base cermets[J].Journal of Solid State Chemistry,2006,179:2809. |
| [7] | 王永国,李兆前,黄传真,张涛,刘福田.三元硼化物基金属陶瓷的研究进展[J].材料导报,2001(09):9-11. |
| [8] | 周小平,胡心彬,王钰.反应火焰喷涂三元硼化物金属陶瓷涂层的组织和性能[J].表面技术,2009(02):7-9. |
| [9] | 殷秀银,吴玉萍,林龙,王涛,卢文欢.等离子喷涂工艺参数对FeCrBSi合金涂层结合强度的影响[J].理化检验-物理分册,2009(08):478-482. |
| [10] | 穆柏春;刘秉余 .Research on the ceramic coating on metallic surface made by chemical reac-tion method(金属表面化学反应陶瓷涂层的研究)[J].硅酸盐通报,1997,6:19. |
| [11] | 承新,郑勇,于海军,卜海建,严永林,赵能伟.三元硼化物基金属陶瓷的研究进展[J].材料导报,2007(07):52-54,58. |
| [12] | 赵正,刘福田,李文虎.Mo2FeB2硬质合金覆层材料的耐磨损性能[J].硅酸盐学报,2008(z1):95-98. |
| [13] | 王永国,李兆前,曹元,张涛.硬质覆层材料的磨损性能研究[J].机械工程材料,2002(04):30-31,34. |
| [14] | 于惠博,孙宏飞,武彬,刘美淋.降低涂层孔隙率的研究进展[J].材料导报,2007(01):68-71. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%