对Gd2Zr2O7与Al2O32层陶瓷材料在1600℃下的高温界面反应行为进行了研究.采用XRD,SEM,EDX等分析手段分析了反应生成的界面相成分和形貌,同时对该反应层的形成机理进行了研究.结果表明,界面反应层的相成分主要为GdAlO3;GdAlO3的形成机理是:在Al2O3存在的前提下,Gd2Zr2O7分解成Gd2O3和ZrO2,Gd2O3与Al2O3反应形成GdAlO3.
参考文献
[1] | Clarke D R;Levi C G .[J].Annual Review of Materials Research,2003,33:383. |
[2] | Ulrich Bast;Eckart Schumann .Development of novel oxide materials for TBC's[J].Ceramic Engineering and Science Proceedings,2002(4):525-532. |
[3] | Wu J;Wei X;Padture N P et al.[J].Journal of the American Ceramic Society,2002,85(12):3031. |
[4] | Vassen R.;Cao X. .Zirconates as New Materials for Thermal Barrier Coatings[J].Journal of the American Ceramic Society,2000(8):2023-2028. |
[5] | Maloney M J .[P].US:6117569,2000. |
[6] | Maloney M J .[P].US:6284323,2001. |
[7] | 刘燕祎 等.[J].稀有金属材料与工程,2003,33(z1):58. |
[8] | Xu Q;Pan W;Wang J et al.[J].Key Engineering Materials,2005,280-283:1507. |
[9] | Evans A G;Mumm D R;Hutchinson J W et al.[J].Progress in Materials Science,2001,46:505. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%