对[(Fe1-xCox)0.75B0.2Si0.05]96Nb4(x=0.1、0.2、0.3、0.4)金属玻璃在1kHz~15MHz间的磁谱进行了研究,该系列金属玻璃的磁谱是典型的德拜型谱线.由于钴元素的添加,表现出较高的弛豫频率(f0)和较高的电阻率(ρRT),但是复数磁导率实部幅值降低.当x=0.4时,弛豫频率达到最大值1.1×106Hz.电阻率随着钴元素加入从212μΩ·cm增加到272μΩ·cm.
参考文献
[1] | Schwarz RB;Shen TD;Harms U;Lillo T .Soft ferromagnetism in amorphous and nanocrystalline alloys[J].Journal of Magnetism and Magnetic Materials,2004(2/3):223-230. |
[2] | Inoue A.;Mizushima T.;Makino A. .SOFT MAGNETIC PROPERTIES OF FE BASED AMORPHOUS THICK SHEETS WITH LARGE GLASS FORMING ABILITY[J].Journal of Applied Physics,1997(8 Pt.2a):4029-4031. |
[3] | Mizushima T.;Inoue A.;Makino A. .Influence of Si addition on thermal stability and soft magnetic properties for Fe-Al-Ga-P-C-B glassy alloys[J].Journal of Applied Physics,1998(11 Pt.2):6329-6331. |
[4] | Shen T D;Schwarz R B .[J].Applied Physics Letters,1999,75:49-51. |
[5] | Koshiba H;Inoue A;Makino A .[J].Journal of Applied Physics,1999,85:5136-5138. |
[6] | Chiriac H.;Lupu N. .Bulk amorphous (Fe, Co, Ni)(70)(Zr, Nb, M)(10)B-20 (M = Ti, Ta or Mo) soft magnetic alloys[J].Journal of Magnetism and Magnetic Materials,2000(0):394-396. |
[7] | Long Y;Zhang Wei;Wang Xinmin et al.[J].Journal of Applied Physics,2002,91:5227-5229. |
[8] | Shen B;Inoue A;Chang C .[J].Applied Physics Letters,2004,85:4911-4913. |
[9] | Bitoh T;Makino A;Inoue A .[J].Journal of Applied Physics,2006,99:08F102-08F103. |
[10] | Macdonald J R.Impedance Spectroscopy[M].New York:wiley,1987 |
[11] | GB/T 19345-2003.GB/T 19345-2003.非晶、纳米晶软磁合金带材[S]. |
[12] | Cullity B D.Introduction to Magnetic Materials[M].MA:Addison-Wesley,1972:446. |
[13] | Vella-Coleiro G P;Smith D H;van Uitert L G .[J].Journal of Applied Physics,1972,43:2428-2430. |
[14] | Aguilar-Sahagun G;Quintana P;Amano E et al.[J].Journal of Applied Physics,1994,75:7000-7002. |
[15] | Allia P;Beatrice C;Vinai F et al.[J].Applied Physics Letters,1987,51:142-144. |
[16] | Mao Xingyu;Gao Wenli;Tang Jianchen et al.[J].Journal of Magnetism and Magnetic Materials,2004,271:286-289. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%