采用真空非自耗+真空自耗电弧熔炼的方法制备了Nb-Cr系多元合金的母合金锭;对母合金进行了1450℃,24h+1000℃,24h的热处理;采用三点弯曲方法测试了合金的室温断裂韧性;进行了950℃不同时间的氧化实验.发现热处理后Nbss基体由树枝晶转变为等轴晶,而Laves相Cr2(Nb,Ti,Hf)则由块状转变为边界圆润的棒状;合金的室温断裂机制由电弧熔炼态的解理断裂转变为热处理后的准解理断裂;950℃的氧化产物为CrNbO4、HfO2、TiO2、CrNb11O29和Ti2Nb10O29.
参考文献
| [1] | 傅恒志.未来航空发动机材料面临的挑战与发展趋向[J].航空材料学报,1998(04):52. |
| [2] | Chan K S;Davidson D L .[J].Journal of the Minerals,Metals & Materials Society,1996,9:62. |
| [3] | Thoma D J;Nibur K A;Chen K C et al.[J].Materials Science and Engineering,2002,A329:408. |
| [4] | Takeyama M;Liu C T .[J].Materials Science and Engineering,1991,A132:61. |
| [5] | Chan K S .[J].Materials Science and Engineering,2002,A329:513. |
| [6] | Davidson D L .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1997,28A(06):1297. |
| [7] | Ohta T.;Nakagawa Y.;Kaneno Y.;Inoue H.;Takasugi IT.;Kim WY. .Microstructures and mechanical properties of NbCr2 and ZrCr2 Laves phase alloys prepared by powder metallurgy[J].Journal of Materials Science,2003(4):657-665. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%