采用铌铁矿预产物合成法制备La掺杂Pb(1-x)Lax(Mg1/3 Nb2/3)0.75Ti0.25O3(0.75PMN-0.25PT-xLa,x=0、0.01、0.015、0.02)铁电陶瓷,并研究了不同含量La掺杂对PMN—PT的微观结构及其性能的影响.结果表明,所有陶瓷样品均为纯钙钛矿结构,没有其他任何杂相,而且随La含量的增加,材料相结构逐渐由三方相向四方相转变.当La掺杂量为0.015时,0.75PMN-0.25 PT-xLa陶瓷出现三方和四方相共存现象,即出现了准同型相界(MPB),使得0.75PMN-0.25PT-xLa陶瓷的电学性能得到了较大的提高,压电常数d33~ 360 pC/N,介电常数εr~6000.La掺杂量达到0.02时,材料的相结构已全部转化为四方相,提高了晶体的对称性,为制备La掺杂0.75PMN-0.25PT电光透明陶瓷提供了依据.

参考文献

[1] 曹林洪,姚熹,徐卓.准同型相界附近PMN-PT陶瓷的介电与压电性能[J].材料热处理学报,2007(03):1-5.
[2] Linhong Cao;Xi Yao;Zhuo Xu .Effect of Ta substitution on microstructure and electrical properties of 0.80Pb(Mg_(1/3)Nb_(2/3))O_3-0.20PbTiO_3 ceramics[J].Ceramics International,2004(7):1369-1372.
[3] 孙大志,赵梅瑜,罗豪甦,瞿翠凤,金绮华,姚春华,林盛卫,殷之文.PMNT陶瓷材料的压电介电性能研究[J].无机材料学报,2000(05):939-942.
[4] 曹林洪,姚熹,徐卓.锂盐助烧铌镁酸铅-钛酸铅陶瓷的压电性能[J].硅酸盐学报,2008(06):756-759,764.
[5] Yun-Han Chen;Kenji Uchino;Dwight Viehland .Substituent effects in 0.65Pb(Mg{sub}(1/3)Nb{sub}(2/3))O{sub}(3-0.35)PbTiO{sub}3 piezoelectric ceramics[J].Journal of electroceramics,2001(1):13-19.
[6] H.Yamada .Pressureless sintering of PMN-PT ceramics[J].Journal of the European Ceramic Society,1999(6/7):1053-1056.
[7] 王歆,庄志强.PMN-PT弛豫铁电粉体和薄膜的无机盐-凝胶法制备[J].硅酸盐学报,2002(z1):68-71,82.
[8] Xiaohua Fang;Bingquan Li;Huiming Gu .Low-temperature single-step reactive sintering methods for lead magnesium niobate[J].Materials Letters,2005(26):3262-3266.
[9] Wei Ruan;Guorong Li;Jiangtao Zeng;Jianjiang Bian;Liudmila S. Kamzina;Huarong Zeng;Liaoying Zheng;Aili Ding .Large Electro-Optic Effect in La-Doped 0.75Pb(Mg_(1/3)Nb_(2/3))O_3-0.25PbTiO_3 Transparent Ceramic by Two-Stage Sintering[J].Journal of the American Ceramic Society,2010(8):2128-2131.
[10] Wei Ruan;Guorong Li;Jiangtao Zeng;Jianjiang Bian;Liudmila S. Kamzina;Huarong Zeng;Liaoying Zheng;Aili Ding .Large Electro-Optic Effect in La-Doped 0.75Pb(Mg_(1/3)Nb_(2/3))O_3-0.25PbTiO_3 Transparent Ceramic by Two-Stage Sintering[J].Journal of the American Ceramic Society,2010(8):2128-2131.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%