研究了在昆钢特有的双机架紧凑式炉卷轧机上开发和生产高强度汽车大梁钢K610L的工艺。通过合理的Nb-Ti复合成分设计和各工序生产工艺试验与优化,生产出满足重型载货汽车制造厂要求的K610L高强度汽车大梁钢。结果表明,昆钢利用炉卷轧机生产的K610L具有较高的抗拉强度、良好的韧性、优异的冷弯成型性能和较好的自然时效性。
Process of developing and producing high strength steel for automobile frames（K610L） by the compact double stands Steckel mill,which owned only by KISC（Kunming Iron and Steel Group Co.,Ltd.）,was investigated.Reasonable Nb-Ti micro-alloying compositions and optimizing production process were designed.The results show that the K610L has not only high strength,good ductility,excellent cold formability,but also good natural aging performance,which is suitable to the higher requirements of automobile frames for developing heavy duty trucks in the truck manufacture plant.
参考文献
| [1] | 董瑞峰,王雪莲,闫波.包钢CSP铌微合金化汽车大梁用钢板的研制[J].轧钢,2006(01):8-10. |
| [2] | 毛新平,王中丙,林振源,许传棻,康永林,傅杰.电炉CSP流程低碳高强汽车大梁钢的开发[J].钢铁,2005(02):37-40. |
| [3] | 杜林秀,张中平,余广夫,马金龙,刘相华,王国栋.低成本590 Mpa级汽车大梁钢板的工业试制[J].金属热处理,2007(12):42-44. |
| [4] | 刘仁东,孟贝,刘凤莲,黄大鹏,王轶,杨海峰,孙群,关菊.鞍钢高强汽车大梁板A610L的开发与研制[J].汽车工艺与材料,2004(06):51-53. |
| [5] | 盖世文,张九皋.TIPPINS双机架紧凑式炉卷轧机的技术评价[J].四川冶金,2003(01):23-25. |
| [6] | Thillou V;Hua M;Garcia C I et al.Precipitation of NbC and Effect of Mn on the Strength Properties Hot Strip HSLA Low Carbon Steel[J].Materials Science Forum,1998,284-286:313. |
| [7] | 范敬国,赵征志,ZHAO Aimin,赵爱民.铌钛微合金化汽车大梁板510L开发[J].热加工工艺,2009(08):21-24. |
| [8] | 王权,周明君,李晓春,付学义,张丽颖.轧制工艺及时效时间对大规格高碳钢线材性能的影响[J].金属热处理,2002(07):15-18. |
| [9] | 完卫国,赵明琦.热轧带肋钢筋时效后拉伸性能变化的研究[J].理化检验-物理分册,2005(06):275-279. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%