在多层压电器件的研制过程中，为实现压电陶瓷和Ａｇ／Ｐｄ内电极的共烧结，本文对中温１１００～１１４０℃范围烧成的ＰＺＮ－ＰＺ－ＰＴ系压电陶瓷的电性能进行了研究，结果表明，保温时间对该组成的压电介电性能有重要的影响，随保温时间的延长，ｄ３３从４２０×１０－１２Ｃ／Ｎ增加到 ５６０×１０－１２Ｃ／Ｎ， εＴ３３从 ２１８０增加到 ２９００。
In order to realize the co-sintering with Ag/Pd electrodes in multilayer devices, PZNPZT piezoelectric ceramics were prepared by a conventional technique in the sintering temperature range from 1100℃ to 1140℃ and their piezoelectric and dielectric properties were carefully studied. The results show that soaking time is the most important factor concerning with piezoelectric and dielectric properties, d33 increases from 420× 10-12C/N to 560× 10-12C/N and εT33 increases from 2100 to 2900 with the increase of soaking time.
参考文献
| [1] | Takahashi S. Jpn. J. Appl. Phys., 1980, 19 (4): 771--772. [2] Wittmer D, Buchanan R C. J. Am. Ceram. Soc., 1981, 64 (8): 485--490. [3] Fu S L, Wei C C, Cheng S Y, et al. Int. J. Hybrid Microelectronics, 1985, 8: 1. [4] Palmour H. Proc. 6th World Round Table Conference on Sintering, Herceg-Novi, Yugoslavia, 1985. 17--34. [5] Gui Z L, Li L T, Gao S H, et al. J. Am. Ceram. Soc., 1989, 72 (3): 386--391. [6] Wang X L, Yao X. Ferroelectrics, 1997, 196: 195--198. [7] Hu Y. J. Mater. Sci., 1996, 31: 4225--4259. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%