采用水基溶胶-凝胶工艺成功地制备了成分均匀的Ba0 7Sr0.3TiO3/Si铁电薄膜.利用光镜、SEM、TEM、XRD等手段对溶胶-凝胶和薄膜的结构、形貌进行了表征,分析了水解聚合过程和水解程度对溶胶-凝胶产物的影响,研究了工艺条件对薄膜质量的影响,讨论了热处理条件对薄膜结晶性能的影响.研究结果表明,采用较高浓度的水基前驱体,有利于薄膜的形成和均匀性.溶胶浓度0.56 mol/L,pH值5.5,陈化时间48～72 h,可以获得较好质量的薄膜;XRD分析表明薄膜650℃处理后已经形成了钙钛矿相的结构.
参考文献
| [1] | Kong LB.;Ma J. .Randomly oriented Bi4Ti3O12 thin films derived from a hybrid sol-gel process[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(1/2):89-93. |
| [2] | Lchinose N;Ogiwara T .[J].Japanese Journal of Applied Physics,1993,32(9B):4115. |
| [3] | Ruckenbauer V.;Hau FF.;Lu SG.;Yeung KM.;Mak CL.;Wong KH. .Characteristics of BaxSr1-xTiO3 thin films grown by pulsed laser ablation of rotating split targets of BaTiO3 and SrTiO3[J].Applied physics, A. Materials science & processing,2004(7):1049-1052. |
| [4] | 符春林,杨传仁,陈宏伟,胡文成,李文远.钛酸锶钡（BST）薄膜的制备与应用研究进展[J].电子元件与材料,2003(05):47-50. |
| [5] | Yi G H;Michael S .[J].Journal of Sol-Gel Science and Technology,1996,6(01):65. |
| [6] | 齐兵;何夕云;丁爱丽 et al.[J].无机材料学报,1998,13(03):389. |
| [7] | 何夕云;丁爱丽;仇萍荪 et al.[J].功能材料,1999,30(04):394. |
| [8] | 符连社;张洪杰;邵华 et al.[J].材料科学与工程,1999,17(01):84. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%