为进一步提高热镀锌铝钢三价铬钝化膜的耐蚀性,分别或同时向三价铬钝化液中加入Co(Ⅱ)、硅溶胶进行钝化,通过中性盐雾试验、极化曲线测试及形貌观察、成分分析,考察了硅溶胶、Co(Ⅱ)盐对三价铬磷酸盐钝化膜耐蚀性的影响,考察两者的协同效应.结果表明:硅溶胶和Co(Ⅱ)盐的加入均能有效提高三价铬钝化膜的耐蚀性,两者同时添加时转化膜耐蚀性更好;硅溶胶的加入对钝化膜起到了很好的填充作用,少量Co(Ⅱ)盐使膜层表面晶格歪曲,抑制活性点的过度生长,可防止尖刺生成;同时添加Co(Ⅱ)和硅溶胶的三价铬钝化液所得的钝化膜中磷酸锌、磷酸铝生成时伴随磷酸铬和磷酸钴生成,二氧化硅在最外层,后期填充形成外表层,表层同时有一定量的磷酸锌.
参考文献
| [1] | Fonte B D,Clemens J M.Trivalent Chromium Passivate Solution and Process:US,4359345[P].1982-11-16.,1982. |
| [2] | Huvar R J,Arbor A M.Trivalent Chromium Passivate Solution and Process:US,4349392[P].1982-09-14.,1982. |
| [3] | Crotty D E,Park H.Non-Peroxide Trivalent Chromium Passivate Composition and Process:US,4578122[P].1986-03-25.,1986. |
| [4] | Ramezanzadeh B,Attar M M,Farzam M .Corrosion performance of a hot-dip galvanized steel treated by different kinds of conversion coatings[J].Surface and Coatings Technology,2010,205(3):874~884.,2010. |
| [5] | 彭天兰,满瑞林.镀锌钢板表面乙烯基三甲氧基硅烷化处理[J].材料科学与工程学报,2009(02):222-224. |
| [6] | 蒋建忠,缪树婷,郝利峰,韩生.镀锌层三价铬钝化及钝化膜的封闭处理[J].电镀与涂饰,2013(10):43-46. |
| [7] | 郭晓斐,王玥,孙华,王璐,修先文.镀锌层三价铬钝化膜的制备工艺及性能研究[J].材料保护,2012(02):35-37,48. |
| [8] | 张永,张金生,阮欢欢,等 .纳米SiO2在镀锌层三价铬钝化中的作用[J].材料保护,2011,44(11):45~47.,2011. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%