The stress rupture properties of a single crystal superalloy were tested at 975°C/255MPa as a function of the deviation degrees from [001]. The misorientation of the specimens away from [001] distributed approximately along a line between [001]-[011] and [001]-[-111] boundaries in the triangle of the stereographic projection. Creep rupture lifetimes of the specimens were not sensitive to the misorientation until the deviation degree exceeded ~30°. Two steps of lattice rotation were found in all specimens during creep, first towards the [001]-[-111] boundary, and then to [001] or [-111] along the boundary. Single slip and strong asymmetric deformation were observed during the first stage of lattice rotation in specimens with large misorientation. The rotation mechanism was associated with the activated slip systems according to the calculated Schmid factors. The impact of lattice rotation on the rupture properties was also discussed.
参考文献
| [1] | D.N. Duhl: Superalloys II, eds C.T. Sims, N.S. Stoloff and W.C. Hagel, John Wiley and Sons, New York, 1987.[2 ] A.D. Cetel and D.N. Duhl: Superalloys 1988, eds S. Reichman, D.N. Duhl, G. Maurer, S. Antolovich and C. Lund, TMS-AIME, Warrendale, PA, 1988, 235.[3 ] E.W. Ross and K.S. O'Hara: Superalloys 1996, eds R.D. Kissinger, D.J. Bye, D.L. Anton, A.D. Cetel, M.V. Nathal, T.M. Pollock and D.A.Woodford, TMS-AIMS, Warrandale, PA, 1996, 19.[4 ] R.C. Reed: Superalloys: Fundamentals and Applications, Cambridge University Press, Cambridge, 2006, 139.[5 ] A.F. Giamei and B.H. Kear: Metall. Trans., 1970, 1, 2185.[6 ] T.M. Pollock, W.H. Murphy, E.H. Goldman, D.L. Uram and J.S. Tu: Superalloys 1992, eds S.D. Antolokch, R.W. Stusrud, R.A. MacKay, D.L. Anton, T. Khan, R.D. Kissinger and D.L. Klarstrom, TMS,Warrendale, PA, 1992, 125.[7 ] T.M. Pollock: Mater. Sci. Eng. B, 1995, 32, 255.[8 ] T.M. Pollock and W.H. Murphy: Metall. Mater. Trans. A, 1996, 27, 1081.[9 ] A.K. Sample and A. Hellawell: Metall. Trans. A, 1984, 15, 2163.[10] S.M. Copley, A.F. Giamei, S.M. Johnson and M.F. Hornbecker: Metall. Trans., 1970, 1, 2193.[11] B.H. Kear and G.R. Leverant: Metall. Trans., 1970, 1, 491.[12] R.A. Mackay and R.D. Maier: Metall. Trans. A, 1982, 13, 1747.[13] T.M. Pollock and R.D. Field: Dislocations in Solids, Elsevier, Amsterdam, 2002, 567.[14] C.M.F. Rae, N. Matan and R.C. Reed: Mater. Sci. Eng. A, 2001, 300, 125.[15] C.M.F. Rae and R.C. Reed: Acta Mater., 2007, 55, 1067.[16] G.R. Leverant, B.H. Kear and J.M. Oblak: Metall. Trans., 1973, 4, 355.[17] N. Matan and D.C. Cox: Acta Mater., 1999, 47, 1549.[18] V. Sass, U. Glatzel and M. Feller-Kniepmeier: Acta Mater., 1996, 44, 1967.[19] V. Sass and M. Feller-Kniepmeier: Mater. Sci. Eng. A, 1998, 245, 19.[20] J.L. Liu , T. Jin, X.F. Sun, J.H. Zhang, H.R. Guan and Z.Q. Hu: Mater. Sci. Eng. A, 2007, 479, 277.[21] B. Reppich: Acta Metall., 1982, 30, 87.[22] B. Reppich: Acta Metall., 1982, 30, 95.[23] E. Nembach, K. Suzuki, M. Ichihara and S. Takeuchi: Philo. Mag. A, 1985, 51, 607.[24] C.M.F. Rae, N. Matan, D.C. Cox, M.A. Rist and R.C. Reed: Metall. Mater. Trans. A, 2000, 31, 2219.[25] L.M. Pan, I. Scheiblp, M.B. Henderson, B.A. Shollock and M. McLean: Acta Metall. Mater., 1995, 43, 1375.[26] D.M. Shah, S. Vega, S. Woodard and A.D. Cetel: Superalloys 2004, eds K.A. Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra and S. Walston, TMS, Warrendale, PA, 2004, 197.[27] V. Sass, W. Schneider and H. Mughrabi: Scripta Metall. Mater., 1994, 31, 885.[28] T.M. Pollock and A.S. Argon: Acta Metall. Mater., 1992, 40, 1.[29] A. Hopgood and J.W. Martin: Mater. Sci. Eng., 1986, 82, 27.[30] R.A. Mackay, R.L. Dreshfield and R.D. Maier: Superalloys 1980, eds J.K. Tien, S.T. Wlodek, H. Morrow III, M. Gell and G.E. Maurer, TMS, Warrendale, PA, 1980, 385. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%