研究了一种以甲酸、乙酸及第三种配位剂组合的三价铬电镀工艺,并对该镀液和镀层进行了性能测试.测试结果显示,该体系所得镀层外观光泽明亮,光亮电流密度范围宽(可使用的电流密度从2.5～25.0 A/dm2);镀液的pH值容易控制,分散能力和覆盖能力好,可在室温下电镀,镀液性能比较稳定;通过Tafel测试和CASS试验证明,三价铬镀铬层的耐蚀性和六价铬镀层相当.
参考文献
| [1] | El Sharif M;Chisholm C V .Characteristics of Electrodeposited Chromium[J].Transactions of the Institute of Metal Finishing,1997,75(06):208. |
| [2] | Jamese H,Lindsay.Decorative and Hard Chromium Plating[J].Plating and Surface Finishing,2004(08):16. |
| [3] | 杨哲龙,屠振密,张景双,安茂忠.三价铬电镀的新进展[J].电镀与环保,2001(02):1-3. |
| [4] | Ibrahim S K;Watson A;Gawne D T .The Role of Formic Acid and Methanol on Speciation Rate and Quality in the Electro-Deposition of Chromium from Trivalent Electrolytes[J].Transactions of the Institute of Metal Finishing,1997,75(05):181. |
| [5] | Tu Z M;Yang Z L .Cathode Polarization in Trivalent Chromium Plating[J].Plating and Surface Finishing,1993,79(09):78. |
| [6] | Song Y B;Chin D T.Current efficiency and polarization behavior of trivalent chromium electrodeposition process[J].Electrochimica Acta,2002(48):349. |
| [7] | Duan S;Li H;Zhang X et al.Hard chromium plating from a trivalent plating bath[J].Plating and Surface Finishing,1995,82(06):84. |
| [8] | Ibrahim K;Watson A .Corrosion and Wear Resistance of Thick Chromium Deposits from Accelerated Cr (Ⅲ) Electrolytes[J].Transactions of the Institute of Metal Finishing,1998,76(04):156. |
| [9] | Smith M A;Watson A;Vaughan D H .The Role of Oligomeric Olated Species in the Deposition Rate of Chromium form a Commercial Chromium (Ⅲ) Electrolyte[J].Tans IMF,1993,71(03):106. |
| [10] | Hong G;Siow K S;Zhigiang G.Hard chromium plating from trivalent[J].Plating and Surface Finishing,2001(03):69. |
| [11] | Baral A;Engelken R .Modeling,optimization fand comparative analysis of trivalent electrodeposition from aqueous glycine and formic acid baths[J].Journal of the Electrochemical Society,2005,152(07):C504. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%