矿物掺合料的引入会减少水泥砂浆内部碱性物质含量,同时其中的活性成分与氢氧化钙发生二次水化反应,进一步地减少了砂浆的碱性,从而降低了砂浆的抗碳化能力.本文通过热重-差示扫描量热试验研究了不同掺量粒化高炉矿渣引入对碳化产物和微观结构的影响.研究结果表明:喷洒酚酞指示剂显示为无色的碳化表层仍然存在少量的Ca (OH)2,这说明砂浆碳化存在部分碳化区;碳化反应物不仅包含Ca(OH)2,也包含水化硅酸钙凝胶(CSH gel),钙矾石(AFt),低硫型水化硫铝酸钙(AFm),硅酸二钙(C2S),硅酸三钙(C3S)等物质;此外,随着矿渣含量的提高,碳化速率增大,同时由于矿渣可以改善水泥浆体的孔结构,矿渣掺量在50％时,碳化速率最小.
参考文献
| [1] | Yoon IS;Copuroglu O;Park KB .Effect of global climatic change on carbonation progress of concrete[J].Atmospheric environment,2007(34):7274-7285. |
| [2] | T. Saeki;P.J.M. Monteiro .A model to predict the amount of calcium hydroxide in concrete containing mineral admixtures[J].Cement and Concrete Research,2005(10):1914-1921. |
| [3] | Gao Yingli;Cheng Ling;Gao Zheming;Guo Shiying .Effects of different mineral admixtures on carbonation resistance of lightweight aggregate concrete[J].Construction and Building Materials,2013(Jun.):506-510. |
| [4] | Elke Gruyaert;Philip Van den Heede;Nele De Belie .Carbonation of slag concrete: Effect of the cement replacement level and curing on the carbonation coefficient - Effect of carbonation on the pore structure[J].Cement & concrete composites,2013(1):39-48. |
| [5] | Paulo H.R. Borges;Juliana 0. Costa;Neil B. Milestone .Carbonation of CH and C-S-H in composite cement pastes containing high amounts of BFS[J].Cement and Concrete Research,2010(2):284-292. |
| [6] | A. Bouikni;R.N. Swamy;A. Bali .Durability properties of concrete containing 50% and 65% slag[J].Construction and Building Materials,2009(8):2836-2845. |
| [7] | Xiong Zhang;Keru Wu;An Yan .Carbonation property of hardened binder pastes containing super-pulverized blast-furnace slag[J].Cement & concrete composites,2004(4):371-374. |
| [8] | P. Sulapha;S. F. Wong;T. H. Wee;S. Swaddiwudhipong .Carbonation of Concrete Containing Mineral Admixtures[J].Journal of Materials in Civil Engineering,2003(2):134-143. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%