运用触点材料测试系统进行了AgSnO2电接触材料在低压直流条件下的电接触实验，研究了材料转移情况，分析了电弧侵蚀形貌和成分变化。结果表明：AgSnO2(12)的转移方向为阴极向阳极转移，阴、阳极材料转移速率均为初期较快后逐渐减缓。阴、阳极表面可按电弧侵蚀形貌分成对应的三个圆环状区域：中心A区—电弧作用域，B区—电弧影响区，最外层区—电弧无明显影响区。阴极电弧作用区微观形貌主要为海绵状基体上分布着大小不一的孔洞，Sn 和 O 元素多偏聚在孔洞区域；阳极侵蚀区主要为熔融流动铺层或喷溅状态。
Electricalcontactexperiment systems wereused to analyze the materialtester on AgSnO2 electricalcontactmaterialsundertheDCload. ThesurfaceprofilesandthemicrostructuresofAgSnO2were observed and measured by SEM and EDS after the test. The results reveals a trend of material transferring fromcathodetoanode on AgSnO2(12) contactmaterials.Thesurfaceofthecathodeandanodecanbedivided into three circular rings according to the arc erosion morphology. The microstructure of cathode is composed primarilyofspongymatrixandtheholeswithdifferentsizesdistributed onit.Anode’morphologyis composed primarily of molten flow layer and splash state.
参考文献
| [1] | 于朝清,刘雪梅,任小梅,徐永红,章应,田茂江,周晓荣.AgSnO2电接触材料制造技术的研究进展[J].贵金属,2014(z1):93-99. |
| [2] | 朱艳彩;王景芹;安立强 等.添加稀土氧化物对电接触材料抗熔焊性能的影响[J].河北工业大学学报,2014,43(3):16-20. |
| [3] | 王松,谢明,柳青,程勇,刘满门,王塞北.内氧化法制备银氧化锡电接触材料[J].电工材料,2014(4):3-6,11. |
| [4] | 王松,陈永泰,杨有才,张吉明,刘满门,王塞北,谢明.AgSnO2电接触材料的研究进展[J].贵金属,2013(z1):102-107. |
| [5] | 任龙霞,吴为麟.虚拟仪器在低压电弧故障断路器研制中的应用[J].电力系统保护与控制,2011(05):134-138,143. |
| [6] | 王海涛,王景芹,朱艳彩.Bi对AgSnO2触头材料接触电阻的影响[J].电工技术学报,2014(5):265-270. |
| [7] | 乔秀清,杨辉,陈乐生,吴新合,穆成法,樊先平,申乾宏.Bi掺杂AgSnO2（12）电接触材料的制备及性能研究[J].电工材料,2013(03):1-5. |
| [8] | 王海涛,王景芹,杜江,孟凡青.稀土对AgSnO2触头材料润湿性影响[J].稀有金属材料与工程,2014(08):1846-1849. |
| [9] | 周晓龙,曹建春,于杰,陈敬超,杜焰.AgMeO电触头材料显微组织均匀化的有效手段--累积挤压大变形技术[J].电工材料,2013(01):20-23. |
| [10] | 张琪,叶凡,黄锡文,刘心宇,张小文,徐涛,陈光明.高能球磨对AgSnO2电触头材料组织与性能的影响[J].稀有金属材料与工程,2015(05):1293-1296. |
| [11] | 熊庆丰,王松,谢明,陈永泰,张吉明,王塞北.用放电等离子烧结技术制备AgSnO2电接触材料[J].贵金属,2013(04):12-16. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%