用电子显微镜和X射线能谱分析等技术对薄板坯连铸连轧CSP工艺生产的低碳钢进行了系统研究,在钢中发现了大量尺寸在30～200 nm范围的纳米级硫化物.在实验研究基础上对硫化物在CSP工艺加速冷却条件下的析出行为进行了讨论,提出了低碳钢中纳米尺寸硫化物的固态析出机制.结果表明:降低钢中的碳含量、控制硫含量、加快铸坯的凝固速度和冷却速度,控制硫化物在奥氏体相区析出等是影响纳米尺寸硫化物形成的重要因素.
参考文献
| [1] | Delu Liu,Xiangdong Huo,Yuanli Wang,Xianwen Sun.Aspects of microstructure in low carbon steels produced by the CSP process[J].北京科技大学学报(英文版),2003(04):1-6. |
| [2] | Yaguchi H .Manganese Sulfide Precipitation in Low-carbon Resulfurized Free-machining Steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17A:2080-2083. |
| [3] | Zhiqiang HAN;Kaike CAI;Baicheng LIU .Prediction and Analysis on Formation of Internal Cracks in Continuously Cast Slabs by Mathematical Models[J].ISIJ International,2001(12):1473-1480. |
| [4] | 霍向东 .薄板坯连铸连轧低碳钢的晶粒细化和析出相研究[D].北京科技大学,2003. |
| [5] | Zhongzhu LIU;Kejing GU;Kaike CAI .Mathematical Model of Sulfide Precipitation on Oxides during Solidification of Fe-Si Alloy[J].ISIJ International,2002(9):950-957. |
| [6] | 冯端.金属物理学[M].北京:科学出版社,1990 |
| [7] | 雍岐龙,刘清友,刘苏,程莲萍,杨天武,陈华,钟卫,郝建英.硫化锰在钢中的Ostwald熟化过程的控制性元素的理论分析[J].特殊钢,2004(06):7-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%