采用扫描电子显微镜和电化学交流阻抗谱研究了Q235B、SPA-H钢和2种不同镍、铬及铜含量的耐候钢在模拟海洋大气环境中的耐蚀性。结果表明：在有Cl-存在的环境中,当镍和铜含量都很低时,单独添加铬在腐蚀前期对减缓腐蚀有利,而在后期对腐蚀有促进作用;镍的质量分数小于0.25%时对耐蚀性的影响不起主导作用;电化学交流阻抗试验结果与腐蚀质量损失试验结果一致;4种钢周期浸润腐蚀48h后的锈蚀量都比较少,腐蚀192h后的锈蚀量明显增加。
The corrosion resistance of Q235B,SPA-H steel and two weathering steels with different alloys contents of Ni,Cr and Cu in simulated marine atmosphere environment were studied by scanning electron microscopy and electrochemical impedance spectroscopy.The results show that only adding Cr was beneficial for retarding corrosion in the early stage,but promoting corrosion at the late stage in the environment of Cl-when the Ni and Cu contents were very low.The effect of Ni on corrosion resistance couldn′t afford leading role when the mass fraction of Ni was less less 0.25wt%.The result of electrochemical impedance test was agreement with the result of the corrosion mass loss test.The rusting of the four steels were small after periodical immersed corrosion for 48 h,and the rusting obviously increased after corrosion for 192 h.
参考文献
| [1] | 董瑞峰,王雪莲.集装箱用热轧钢带的研制[J].包钢科技,2004(02):26-29. |
| [2] | 李湘凡,孙华,郜书忠.高强度耐候钢SPA-H的试制[J].特殊钢,2006(01):53-54. |
| [3] | 岳丽杰 .Cu-P-RE耐候钢中稀土行为作用及机理的研究[D].东北大学,2006. |
| [4] | 刘国超,董俊华,韩恩厚,柯伟.Cu、Mn的协同作用对低合金钢在模拟海洋大气环境中腐蚀的影响[J].腐蚀科学与防护技术,2008(04):235-238. |
| [5] | 岳丽杰,陈为公,王龙妹.Cu-P-RE耐候钢的耐蚀性能[J].北京科技大学学报,2009(05):568-572,601. |
| [6] | 郝献超,肖葵,张汉青,董超芳,李晓刚.模拟海洋大气环境下Cu和Cr对耐候钢耐腐蚀性能的影响[J].材料保护,2009(01):21-23,43. |
| [7] | 车马俊,张晖,穆海玲,万兰凤.成分调整对09CuPCrNi耐候钢耐腐蚀性能的影响[J].热加工工艺,2009(14):17-19,24. |
| [8] | 岳丽杰,王龙妹,朴秀玉,徐成海,朱京希.10PCuRE耐候钢耐蚀锈层的电化学特征[J].稀土,2005(05):56-60. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%