通过微波加热包埋渗法在高铌钛铝合金基体上制备了硅化物涂层,微波加热功率2.6 kW,埋渗时间2 h。利用扫描电镜、能谱分析和X射线衍射等手段研究了氧化前后涂层的表面形貌、截面形貌、涂层中元素分布和物相组成。结果表明:涂层外部主要物相为TiSi2和NbSi2,并有少量的Ti5Si3和Nb5Si3相,厚度约为15μm;内侧涂层有大约15μm的富铝层。1000℃下氧化100 h的氧化动力学测试结果表明:高铌钛铝合金渗硅后的抗高温氧化性能、抗剥落性能有了显著提高,其单位面积增重量和剥落量分别是0.5714 mg/cm2和0.7143 mg/cm2,仅为无涂层试样氧化增重量和剥落量的1/22倍和1/59倍。

Silicide coatings on high-Nb containing TiAl(Nb-TiAl) alloy substrate were successfully prepared by microwave heating pack-siliconizing at 2.6 kW for 2 h.The microstructure,composition distribution and phase constituents of the oxidized and unoxidized coatings were analyzed by means of SEM,EDS and XRD.The SEM observation results show that the outer 15 μm layer of the silicide coatings is almost composed of TiSi2 and NbSi2 with a small quantity of Ti5Si3 and Nb5Si3,and the inner layer is Al-rich layer with thickness about 15 μm.Compared with uncoated Nb-TiAl substrate,the weight gain and spallation of silicide coated Nb-TiAl alloy is much smaller after oxidation experiment at 1000 ℃ for 100 h,which are just 1/22 and 1/59 that of the uncoated sample.Thus the high temperature oxidation resistance of Nb-TiAl alloy can be improved further significantly by microwave heating pack-siliconizing.

参考文献

[1] Kimy W .New material by mechanical alloying[J].JOM-Journal of the Minerals Metals and Materials Society,1989,41:25-27.
[2] Yamaguchi M .High temperature intermetallics with particular emphasis on TiAI[J].Materials Science and Technology,1992,8(04):299-305.
[3] 陈国良;林均品.有序金属间化合物结构材料物理金属学基础[M].北京:冶金工业出版社,1999
[4] 张永刚;韩雅芳;陈国良.金属间化合物结构材料[M].北京:国防工业出版社,2001
[5] Nb-TiAl 金属间化合物研究现状[J].材料导报,2000(07):15-17.
[6] 张宁,林均品,王艳丽,陈国良.合金元素Y对高铌TiAl高温合金长期抗氧化性的影响[J].航空材料学报,2006(06):42-45.
[7] X.J. Zhang;Q. Li;S.Y. Zhao;C.X. Gao;L. Wang;J. Zhang .Improvement In The Oxidation Resistance Of A γ-tial-based Alloy By Sol-gel Derived Al_2o_3 Film[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2008(5P1):1860-1864.
[8] M. Goral;L. Swadzba;G. Moskal .Si-modified aluminide coatings deposited on Ti46A17Nb alloy by slurry method[J].Intermetallics,2009(11):965-967.
[9] 肖伟豪,张亮,姜惠仁.Si对TiAl合金高温抗氧化性能的影响[J].北京航空航天大学学报,2006(03):365-368.
[10] 任家松 .新型Nb硅化物基超高温合金的氧化行为及其抗氧化涂层技术研究[D].西北工业大学,2006.
[11] 李明,宋力昕,乐军,宋学平,郭占成.铌表面固体粉末包埋渗硅研究[J].无机材料学报,2005(03):764-768.
[12] 乔彦强,郭喜平.Ti-Nb-Si基高温合金表面包埋Si-Cr共渗涂层的组织[J].材料热处理学报,2010(03):125-131.
[13] 朱日彰;何业东;齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995
[14] 朱日彰.金属腐蚀学[M].北京:冶金工业出版社,1989
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%