在Na2CO3-Na2SiO3溶液中,采用正负不对称交流微弧氧化电源在钛合金上制备出了多孔金红石TiO2薄膜.利用X射线衍射仪(XRD)和扫描电镜(SEM)分别研究了钛合金微弧氧化陶瓷膜的相组成和微观结构,实验结果表明,氧化膜主要由大量金红石和少量锐钛矿TiO2组成;膜表面布满了尺寸不到4μm的小孔,膜截面没有明显的疏松层和致密层之分.对微弧氧化样品在3.5%NaCl溶液中的抗点腐蚀测试表明,阴极峰值电压与样品的耐腐蚀性能密切相关,当阴、阳极峰值电压和处理时间分别为45、320V和30min所制备的钛合金微弧氧化样品其抗点腐蚀能力最强.
参考文献
[1] | Frantsevich I N;Pilyankevich A N;Lavrenko V A.Naukova Dumka[M].Kiev: Russian,1985 |
[2] | Ishikawa Y;Matsumoto A Y .[J].Electrochimica Acta,2001,46(18):2819. |
[3] | Bakovets V V .[J].Inorganic Mater,in Russian,1987,23(07):1226. |
[4] | Yu JG.;Zhao QN.;Zhao XJ. .Photocatalytic activity of nanometer TiO2 thin films prepared by the sol-gel method[J].Materials Chemistry and Physics,2001(1/3):25-29. |
[5] | Shirkhanzadeh M .[J].Nano-Structured Materials,1995,5:33. |
[6] | Wang X H;Zhang F;Li C R et al.[J].Surface and Coatings Technology,2000,128-129:36. |
[7] | Leng YX.;Zeng ZM.;Tian XB.;Yang P.;Huang N.;Zhou ZR.;Chu PK.;Chen JY. .Properties of titanium oxide biomaterials synthesized by titanium plasma immersion ion implantation and reactive ion oxidation[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(0):573-577. |
[8] | Zhu Y C;Ding C X .[J].European Ceramic Society,2000,20:127-132. |
[9] | Yerokhin A L;Nie X;Leyland A et al.[J].Surface and Coatings Technology,1999,122:73. |
[10] | Mishra P R;Shukla P K;Singh A K et al.[J].International Journal of Hydrogen Energy,2003,28(10):1089. |
[11] | Yerokhin A L;Nie X;Leyland A;Matthews A .[J].Surface and Coatings Technology,2000,130:195. |
[12] | Erokhine .[P].US Patent Specification: 5720866,1996. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%