以水为核,OP-10为表面活性剂,环氧树脂为壳,采用原位聚合法,制备出“核-壳”型环氧树脂微球,真空干燥除去水得到中空的环氧树脂微球,并用扫描电子显微镜、红外光谱和热失重对微球进行了表征.扫描电子显微镜结果表明,当OP-10质量分数约为4％、乙二醇初始温度为50℃时,制备的环氧微球具有较好的中空结构;红外光谱结果表明,所制备的环氧树脂中空微球固化较完全;热失重结果表明环氧树脂中空微球在失重10％时的温度为342℃,质量保存率为16％;激光粒度仪测试结果表明,环氧微球粒径分布范围为10 μm～800 μm,体积加权平均粒径为285 μm.
参考文献
| [1] | Wang, C.;Yan, J.;Cui, X.;Cong, D.;Wang, H. .Preparation and characterization of magnetic hollow PMMA nanospheres via in situ emulsion polymerization[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2010(1/3):71-77. |
| [2] | 刘喜宗,李贺军,马托梅,王斌,李克智.原位聚合法制备酚醛树脂空心微球的工艺研究及性能表征[J].高分子学报,2009(07):695-699. |
| [3] | Abdelkader AF;White JR .Curing characteristics and internal stresses in epoxy coatings: Effect of crosslinking agent[J].Journal of Materials Science,2005(8):1843-1854. |
| [4] | Contu, F.;Fenzy, L.;Taylor, S.R. .An FT-IR investigation of epoxy coatings as a function of electrolyte composition[J].Progress in Organic Coatings: An International Review Journal,2012(1/2):92-96. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%