A QUENCHING INDUCED PLANAR DEFECT OF MARTENSITE IN Cu-Zn-Al ALLOY

ZHU Min YANG Dazhi Dalian University of Technology , Dalian , China Lecturer , Dept.of Matedais Engineering , Dalian University of Technology , Dalian , China

Keywords： martensite , null , null

A new kind of planar defect named non-basal plane stacking faults has been studied by using trace analysis and lattice image techniques.It has been found that they are located in (125)_M plane of martensite lattice.By lattice image observation,the non-basal plane stack- ing faults are argued to be induced by two incomplete basal plane stacking faults and may be the results of rapid quenching.The defects are regarded as anomalous structures of martensite.

参考文献

[1]
[2]
[3]
[4]

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
ZHU Min YANG Dazhi Dalian University of Technology Dalian China Lecturer Dept.of Matedais Engineering Dalian University of Technology Dalian China
在百度学术搜索
ZHU Min YANG Dazhi Dalian University of Technology Dalian China Lecturer Dept.of Matedais Engineering Dalian University of Technology Dalian China
在万方数据库搜索
ZHU Min YANG Dazhi Dalian University of Technology Dalian China Lecturer Dept.of Matedais Engineering Dalian University of Technology Dalian China
在CNKI搜索
ZHU Min YANG Dazhi Dalian University of Technology Dalian China Lecturer Dept.of Matedais Engineering Dalian University of Technology Dalian China

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

A QUENCHING INDUCED PLANAR DEFECT OF MARTENSITE IN Cu-Zn-Al ALLOY

参考文献