用草酸腐刻、双环动电位电化学再活化(DL-EPR)及电化学阻抗谱(EIS)3种方法评价了不同温度(550~800℃)退火处理4 h后Incoloy800合金的晶间腐蚀敏感性,研究了退火温度对Incoloy800合金晶间腐蚀敏感性的影响。分别用光学显微镜(OPM)和扫描电子显微镜(SEM)观察了敏化样品经草酸腐刻后的微观结构和DL-EPR测试后的表面形貌。结果表明3种方法评价结果一致,随着退火温度升高,Incoloy800合金的敏化度先增大后减小,在650和700℃下退火4 h后高度敏化,再活化率Ra均大于30%,而在800℃退火4 h后未被敏化。

Susceptibility to intergranular corrosion of Incoloy 800 alloy annealed at various temperatures ranging from 550 ℃ to 800 ℃ for 4 h was investigated by means of electrolytic etching in oxalic acid,double-loop electrochemical potentiodynamic reactivation(DL-EPR) and electrochemical impedance spectroscopy(EIS) technique.The morphology and microstructure of the alloy after DL-EPR test and electrolytic etching in oxalic acid were examined by optical microscope and scanning electron microscopy technique.It is found that some results are observed by the different evaluating technique.It suggests that the susceptibility of Incoloy 800 increases with annealing temperature raised from 550 ℃ to 650 ℃,while a contrary trend is found when the temperature range of 650 ℃ and 800 ℃,resulting from the healing effect incurred by the diffusion of chromium from adjacent grains to chromium-depleted zones.

参考文献

[1] Fulger, M.;Ohai, D.;Mihalache, M.;Pantiru, M.;Malinovschi, V. .Oxidation behavior of Incoloy 800 under simulated supercritical water conditions[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2009(2):288-293.
[2] Esteban GA.;Perujo A.;Sedano LA.;Legarda F.;Mancinelli B.;Douglas K. .Diffusive transport parameters and surface rate constants of deuterium in Incoloy 800[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2002(1):1-6.
[3] Paul AR.;Dharwadkar SR.;Kaimal KNG. .Migration of carbon in Incoloy-800[J].Materials Chemistry and Physics,1998(3):189-194.
[4] R. Dehmolaei;M. Shamaman;A. Kermanpur .Microstructural changes and mechanical properties of Incoloy 800 after 15 years service[J].Materials Characterization,2009(3):246-250.
[5] 桂立丰;吴民达;赵源.机械工程材料测试手册[M].沈阳:辽宁科学技术出版社,2002
[6] H. Sahlaoui;K. Makhlouf;H. Sidhom .Effects of ageing conditions on the precipitates evolution, chromium depletion and intergranular corrosion susceptibility of AISI 316L: experimental and modeling results[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):98-108.
[7] G. H. Aydogdu;M. K. Aydinol .Determination of susceptibility to intergranular corrosion and electrochemical reactivation behaviour of AISI 316L type stainless steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(11):3565-3583.
[8] Green S J;Paine P N .Materials performance in nuclear pressurized water reactor steam generators[J].Nuclear Technology,1981,55:10-29.
[9] Chafely J E;Roberts D J .Steam-generator materials performance in high-temperature gas-cooled reactors[J].Nuclear Technology,1981,55(01):37-49.
[10] H.-E. Buehler;L. Gerlach;O. Greven;W. Bleck .The electrochemical reactivation test (ERT) to detect the susceptibility to intergranular corrosion[J].Corrosion Science,2003(10):2325-2336.
[11] Majidi A P;Streicher M A .The double loop reactivation method for detecting sensitization in AISI 304 stainless steels[J].Corrosion,1984,40:584-593.
[12] Lopez N;Cid M;Puiggali M et al.Application of double loop electrochemical potentiodynamic reactivation test to austenitic and duplex stainlesssteels[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1997,229:123-128.
[13] 高中平;陈范才;赵常就 .动电位再活化法评价晶间腐蚀敏感性的各种判据[J].四川化工与腐蚀控制,1999,2(03):40-44.
[14] 金维松,郎宇平,荣凡,孙力军.EPR法评价奥氏体不锈钢晶间腐蚀敏感性的研究[J].中国腐蚀与防护学报,2007(01):54-59.
[15] 徐菊良,邓博,孙涛,李劲,蒋益明.DL-EPR法评价2205双相不锈钢晶间腐蚀敏感性[J].金属学报,2010(03):380-384.
[16] S. A. M. Refaey;F. Taha;T. H. A. Hasanin .Passivation and pitting corrosion of nanostructured Sn-Ni alloy in NaCl solutions[J].Electrochimica Acta,2006(14):2942-2948.
[17] Pedro de Lima-Neto;Jesualdo P. Farias;Luis Flavio G. Herculano;Helio C. de Miranda;Walney S. Araujo;Jean-Baptiste Jorcin;Nadine Pebere .Determination of the sensitized zone extension in welded AISI 304 stainless steel using non-destructive electrochemical techniques[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(4):1149-1155.
[18] Huang A C;Chang Z Y;Chen C S .The electrochemical behavior of austenitic stainless steel with different degrees of sensitization in the transpassivepotential region in 1 M H2SO4 containing chloride[J].Corrosion Science,2004,46:1501-1513.
[19] 曹楚南;张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002
[20] Gaudett M A;Scully J R .Distributions of Cr depletion levels in sensitized AISI 304 stainless steel and its implications concerning intergranularcorrosion phenomena[J].Journal of the Electrochemical Society,1993,140:3425-3435.
[21] Osozawa K;Bohnenkamp K .Potentiostatic study on the intergranular corrosion of an austenitic chromium-nickel stainless steel[J].Corrosion Science,1966,6:421-433.
[22] A. Pardo;M.C. Merino;A.E. Coy .Influence of Ti, C and N concentration on the intergranular corrosion behaviour of AISI 316Ti and 321 stainless steels[J].Acta materialia,2007(7):2239-2251.
[23] Hall E L;Briant C L .Chromium depletion in the vicinity of carbides in sensitized austenitic stainless steels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1984,15:793-811.
[24] David L;Reichert .A modified double loop EPR technique for detection of sensitization in cast stainless steel[J].Journal of the Electrochemical Society,1990,137:411-413.
[25] Lefu Zhang;Yasuhiro Kamada;Hiroaki Kikuchi .Magnetic transition temperatures of some model alloys for simulating radiation induced segregation in austenitic stainless steel[J].Journal of Magnetism and Magnetic Materials,2004(2/3):402-408.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%