主要介绍了一种先进玻璃纤维增强铝合金复合材料Glare层板的研究进展,并综合分析欧美Glare层板的研究文献,评述了Glare层板的拉伸性能、压缩性能、冲击性能、剪切性能、缺口残余强度、承载强度、疲劳性能等力学性能,分析了Glare层板环境耐久性和阻燃性等稳定性研究.通过与铝合金和Arall层板的性能比较、分析,论述了Glare层板作为替代铝合金应用于飞机制造方面所具有的优异性能及经济性,简单评述了Glare层板铺层结构与性能的关系,为其应用提供评价基础.
参考文献
| [1] | Sinke J .Development of Fibre Metal Laminates: concurrent multi-scale modeling and testing[J].Journal of Materials Science,2006(20):6777-6788. |
| [2] | 梁中全,薛元德,陈绍杰,武文静.GLARE 层板的力学性能及其在A380客机上的应用[C].首届全国航空航天领域中的力学问题学术研讨会论文集,2004:390-392. |
| [3] | Vermeeren C A J R;Beumler T;Dekanter J L C G et al.Glare design aspects and philosophies[J].Applied Composite Materials,2003,10:257. |
| [4] | Sinke J .Manufacturing of glare parts and structures[J].Applied Composite Materials,2003,10:293. |
| [5] | Woerden H J M;Sinke J;Hooijmeijer P A .Maintenance of glare structures and glare as riveted or bonded repair mate-rial[J].Applied Composite Materials,2003,10:307. |
| [6] | Sinke J .Some inspection methods for quality control and in-service inspection of glare[J].Applied Composite Materials,2003,10:277. |
| [7] | Vermeeren C A J R .An historic overview of the development of fibre metal laminates[J].Applied Composite Materials,2003,10:189. |
| [8] | Nikolaos K.Composite patch repair of glare structures[M].Cranfield:Cranfield University,2006 |
| [9] | Laurent F.NDT on A380[A].Orlando(USA),2005:9. |
| [10] | Vogelesang L B.Fiber metal laminates:The development of a new family of hybrid materials[A].Lucern,2003 |
| [11] | Military H .Metallic materials and elements for aerospace vehicle structures[Technical Report MIL-HDBK-5H][R].Department of Defence,USA,1998. |
| [12] | Alderliesten R C;Campoli G;Benedictus R .Modelling cyclic shear deformation of fibre/epoxy layers in fibre metal laminates[J].Journal of Computer Science and Technology,2007,67(11-12):2545. |
| [13] | Vlot A;Gunnink J W.Fibre metal laminates[M].Dordrecht:Kluwer Academic Publishers,2001 |
| [14] | Beumler Th;Starikov R;Gennai A.Controlling the damage with fiber metal laminate structures[A].TU Delft,Netherlands,2007 |
| [15] | ASTMD3039.ASTMD3039.Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials[S].American Society for Testing and Materials,2008. |
| [16] | Bucci R J;Muller L N.Treatise on materials science and technology[M].CA:Academic Press Inc,1989:295. |
| [17] | Gunnink J W;Vogelesang V B.Aerospace Arall:The advancement in aircraft materials[A].Covina,CA,1990 |
| [18] | Gunnink J W;Vogelesang V B.Aerospace Arall:A challenge for the aircraft designer[A].Covina,CA,1991 |
| [19] | Verolme J L .Compressive properties of glare[Report LR-666][R].Delft,Netherlands:Delft University of Technology,1991. |
| [20] | Gegory M A;Roebrocks G.Fiber metal laminate:A solution to weight,strength,and fatigue problems[A].Canada:Ottawa,1991 |
| [21] | Edson C B;Rogério A S;Luiz C P et al.A review on the development and properties of continuous fiber/epoxy/aluminum hybrid composites for aircraft structures[J].Materials Research,2006,9(03):247. |
| [22] | Wu GC;Yang JM;Hahn HT .The impact properties and damage tolerance and of bi-directionally reinforced fiber metal laminates[J].Journal of Materials Science,2007(3):948-957. |
| [23] | Aderliesten R C;Hagenbeek M;Homan J J et al.Fatigue and damage tolerance of glare[J].Applied Composite Materials,2003,10:223. |
| [24] | Liaw B M;Liu L X;Villars E A.Impact damage mechanisms in fiber-metal aminates[A].Portland:Oregon,2001:6. |
| [25] | 程晓林,李文晓,薛元德.单向玻璃纤维-铝合金层板的几种力学性能研究[J].纤维复合材料,2007(03):18-20. |
| [26] | Laliberte F et al.Post-impact fatigue damage growth in fiber-metal laminates[J].J Fatigue,2002,24:249. |
| [27] | ASTMD5379.ASTMD5379.Standard Test Method for Shear Properties of Composite Materials by the V-Notched Beam Method[S].American Society for Testing and Materials,2005. |
| [28] | Hagenbeek M;Van Hengel C;Bosker O J et al.Static properties of fibre metal laminates[J].Applied Composite Materials,2003,10:207. |
| [29] | Wu H F .Use of the rule of mixtures and metal volume fraction for mechanical property predictions of fiber-reinforced aluminum laminates[J].Journal of Materials Science,1994,29:4583. |
| [30] | Devries T J;Vlot A .The influence of the constituent pro-perties on the residual strength of glare[J].Applied Composite Materials,2001,8:263. |
| [31] | Wu G C;Yang J M .The mechanical behavior of glare laminates for aircraft structures[J].Failure Struct Mater,2005,57(01):72. |
| [32] | Gnnink J W;Vlot A;Devries T J et al.Glare technology development 1997-2000[J].Applied Composite Materials,2002,9:201. |
| [33] | Vanrooijen R;Sinke J;Devries T J et al.Property optimi-sation in fibre metal laminates[J].Applied Composite Materials,2004,11:63. |
| [34] | ASTM E238.ASTM E238.Standard Test Method for Pin-Type Bearing Test of Metallic Materials[S].American Society for Testing and Materials,1984. |
| [35] | AS-TMD953.AS-TMD953.Standard Test Method for Bearing Strength of Plastics[S].American Society for Testing and Materials,2002. |
| [36] | Wu H F .An investigation on the bearing test procedure for fiber-reinforced aluminum laminates[J].Journal of Materials Science,1994,29:4592. |
| [37] | Chlupová A;Heger J;Vaek A .Fatigue crack initiation and early growth in glare fiber-metal laminate subjected to mixed tensile and bending loading[J].Acta Polytechnica Scandinavica-Physics Including Nucleonics Series,2001,41:4. |
| [38] | Schijve J;Wiltink F J;Van Bodegom V J W .Flight-simulation tests on notched specimens of fiber-metal laminates[Report LRV-10][R].Delft University of Technology,1994. |
| [39] | ASTM E647.ASTM E647.Standard Test Method for Measurement of Fatigue Crack G-rowth Rates[S].American Society for Testing and Materials,2008. |
| [40] | Hart W G J;Ubels L C .Fatigue and Residual Strength Performance of Glare 4B-5/4-0.4 and 4 mm Thick 2024-T3 after accelerated corrosion testing[NLR-CR-98514][R].National Aerospace Laboratory NLR,1998. |
| [41] | ASTM G34-2001.ASTM G34-2001.Standard Test Method for Exfoliation Corrosion Susceptibility in 2XXX and 7XXX Series Aluminum Alloys (EXCO Test)[S].American Society for Testing and Materials,2001. |
| [42] | Oosting R .Toward a New Durable and Environmentally Compliant Adhesive Bonding Process for Aluminium Alloys[D].Delft:Delft University of Technology,1995. |
| [43] | Roebroeks G H J J.Glare:A structural material for fire resistant fuselages[A].Dresden,Germany,1996 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%