为有效处理和利用固体废弃物,本文研究了用钙系膨胀剂,高炉矿渣水泥以及采用吸水率较小的再生骨料抑制碱骨料反应,尝试制备强度为30 MPa的再生骨料混凝土.并对其耐久性能做了试验研究.试验结果表明:再生骨料混凝土在强度以及耐久性能方面显示出与普通混凝土几乎相同的性能,并用钙系膨胀剂,高炉矿渣水泥以及采用吸水率较小的再生骨料,在解决再生骨料混凝土耐久性方面能够取得较好的效果.
Strength grade C30 of recycled aggregate that was one of effective methods to dispose waste solid was fabricated with Ca series expanding agent, and blast furnace slag cement and low absorption recycled aggregate used to restrain alkali-aggregate reaction.The durable experiment shows that the strength and durability compared ordinary concrete with recycled aggregate concrete both display the same properties and Ca series expanding agent, blast furnace slag cement, and small water absorption play a good effect on durability of recycled aggregate concrete.
参考文献
| [1] | 邓寿昌;王正平;张学兵.建筑固体废弃物的循环利用与再生资源的可持续发展[A].,2007:51-62. |
| [2] | 崔正龙,大芳賀義喜,北迁政文,田中礼治.再生混凝土的冻融循环试验研究[J].建筑材料学报,2007(05):534-537. |
| [3] | (財)国土開発技術開発研究センター[R].建設副産物の発生抑制再利用技術の開発報告書,1994-4. |
| [4] | 肖建庄,雷斌,王长青.汶川地震灾区建筑垃圾的资源化利用[C].首届全国再生混凝土研究与应用学术交流会论文集,2008:63-66. |
| [5] | 日本規格協会.建築関係JIS要覧(試験方法等)[M].新日本法規出版社,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%