采用优化的激光快速成形工艺参数,获得了成形精度得到控制、组织致密的Rene95高温合金力学性能试样.为了提高成形试样的力学性能,对试样进行了固溶+时效热处理.力学性能测试结果表明,成形试样的强度指标已经接近粉末冶金C级标准,塑性指标超过粉末冶金A级标准.试样平均硬度达到HV496.3.
参考文献
[1] | Wohlers Terry T.Worldwide Development & Trends in Rapid Prototyping & Tooling[A].北京:机械工业出版社,1998:20-29. |
[2] | Cawley J D;Heuer A H;Newman W S;Mathewson B B .Computer- aided Manufacturing of Laminated Engineering Materials[J].American Ceramic Society Bulletin,1996,75(05):75. |
[3] | Liu Z E;Ko T C;Best J;Cawley J D, Heuer A H.CAM- LEM Processing: Materials Flexibility[A].Austin:University of Texas at Austin,1997:379. |
[4] | 张永忠,石力开,章萍芝,徐骏.基于金属粉末的激光快速成型技术新进展[J].稀有金属材料与工程,2000(06):361-365. |
[5] | 张永忠,席明哲,石力开,程晶.激光快速成形316L不锈钢的组织及性能[J].稀有金属材料与工程,2002(02):103-105. |
[6] | 涂干云;杨士仲;吴剑涛 .[J].Transactions of Materials and Heat Treatment(金属热处理学报),1997,18(03):23-27. |
[7] | 马培立;陈远亨;丁成林.高温合金低倍图谱[M].北京:机械工业出版社,1986:82. |
[8] | 国为民;宋璞生;吴剑涛 .[J].粉末冶金工业,1999,2(02):9. |
[9] | Griffith M L;Schlienger M E;Harwell L D;Oliver M S,Baldwin M D et al.[J].Materials & Design,1999,20:107. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%