以镀层表面形貌、结合力、抗变色性能和显微硬度为考核指标,采用正交试验法优选了丁二酰亚胺无氰脉冲镀银工艺参数,并与直流条件下的镀银层作了比较.结果表明,脉冲电镀所得镀层表面存在较多微型凹孔,其显微硬度及抗变色性能优于直流镀银层,晶体直径也小于直流镀层;脉冲电流区间略小于直流电镀.镀液分散性稍好于直流电镀.
参考文献
| [1] | 陈春成.无氰镀银技术概况及发展趋势[C].2003年全国电子电镀学术研讨会论文集,2003:118-119. |
| [2] | 刘仁志.无氰镀银的工艺与技术现状[J].电镀与精饰,2006(01):21-24. |
| [3] | 向国朴.脉冲电镀发展概况[J].电镀与涂饰,2000(04):43-47. |
| [4] | 许维源.近年来脉冲电镀发展概况[J].电镀与涂饰,2003(06):41-44,58. |
| [5] | 刘勇,罗义辉,魏子栋.脉冲电镀的研究现状[J].电镀与精饰,2005(05):25-29. |
| [6] | 张宝根;文小和;东树景 .银镀层抗腐蚀变色的测定方法[J].电子电镀,2005,3(02):27-33. |
| [7] | Werle M D;Banakh O;Gay P A et al.Tarnishing resist-anee of silver-palladium thin films[J].Surface and Coatings Technology,2006,200:6696-6701. |
| [8] | Dini J W;Morrissey R J;Pacheco D R .Materials charac-terization of a non-cyanide silver eleetrodeposit[J].Plating and Surface Finishing,1997,84(12):62-67. |
| [9] | Waste Management and Research Center .Non-cyanide sil-ver as a substitute for cyanide Processes[R].Chicago:Chicago Metal Finishers Institute,2002. |
| [10] | Sascha Berger;Gerhard Hoffacker .Novel and Innovative Non-Cyanide Silver process: A report on Commercial Plating Experiences[J].Plating & Surface Finishing,2005(3):46-51. |
| [11] | Blair A .Silver plating[J].Metal Finishing,1999,97(01):298-303. |
| [12] | 屠振密;韩书梅;杨哲龙.肪护装饰性镀层[M].北京:化学工业出版社,2005:339. |
| [13] | 范雄.金属X射线学[M].北京:机械工业出版社,1989:43-47,103-105. |
| [14] | 楚广,唐永建,刘伟,罗江山,杨天足.纳米金属固体材料硬度及强度研究进展[J].湖南有色金属,2005(06):21-24,44. |
| [15] | 王立平,高燕,薛群基,刘惠文,徐洮.电沉积镍纳米晶材料制备及性能[J].电镀与涂饰,2004(03):1-2,5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%