采用80S-G低合金钢焊丝焊接C4镍基合金/X60低合金钢异种金属.利用扫描电镜观察C4镍基合金母材/80S-G焊缝之间熔合区微观组织,能谱分析该区元素分布.结果表明,C4镍基合金母材稀释进入80S-G低合金钢焊缝内,致使Ni、Cr、Mo元素质量分数从部分熔化区到过渡区缓慢降低,Fe元素质量分数增加.微观组织从单相奥氏体组织逐渐转化为奥氏体与铁素体组成的混合组织,在此区域中弥散分布少量析出相粒子.
参考文献
[1] | J.N. DUPONT;C.S. KUSKO .Technical Note: Martensite Formation in Austenitic/Ferritic Dissimilar Alloy Welds[J].Welding Journal,2007(2):51s-54s. |
[2] | Ahmed H. ElSawty .Characterization of the GTAW fusion line phases for superferritic stainless steel weldments[J].Journal of Materials Processing Technology,2001(1/3):128-132. |
[3] | 杨丽颖,柳伟,董小平,路民旭.ECrNiMo-3焊接X60钢部分熔化区组织及腐蚀行为[J].金属热处理,2008(04):84-88. |
[4] | Leonard R B .Thermal stability of Hastelloy alloy C-276[J].Corrosion,1967,25(05):222-228. |
[5] | Raghavan M;Berkowitz B J;Sanlon J C .Electron microscopic analysis of heterogeneous precipitates in Hastetloy C-276[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13(06):979-984. |
[6] | Ogborn J S;Olson D L;Cieslak M J .Influence of solidification on the microstructural evolution of nickel base weld metal[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1995,203(01):134-139. |
[7] | J. N. DuPONT .Microstructural Development and Solidification Cracking Susceptibility of a Stabilized Stainless Steel[J].Welding Journal,1999(7):253s-263s. |
[8] | 黄安国,余圣甫,谢明立,李志远,张国栋.低合金钢焊缝的针状铁素体微观组织[J].焊接学报,2008(03):45-48. |
[9] | Pavlovsk(y) J;Million B;Cíha K;Stránsk(y) K .Carbon redistribution between an austenitic cladding and a ferritic steel for pressure vessels of a nuclear reactor[J].Materials Science and Engineering A,1991,149(01):105-110. |
[10] | Sedat Kolukisa .The effect of the welding temperature on the weldability in diffusion welding of martensitic (AISI420) stainless steel with ductile (spheroidal graphite-nodular) cast iron[J].Journal of Materials Processing Technology,2007(1/3):33-36. |
[11] | 由伟,方鸿生,白秉哲.用反向传播人工神经网络预测低碳低合金钢的马氏体转变开始温度[J].金属学报,2003(06):630-634. |
[12] | A. UL-HAMID;H. M. TAWANCY;N. M. ABBAS .Failure of weld joints between carbon steel pipe and 304 stainless steel elbows[J].Engineering failure analysis,2005(2):181-191. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%