基于一组薄壁微制品的微注塑成型实验,研究不同尺度(100 μm、200 μm、500 μm、1mm)制品的可成型性及充填过程中的流动现象,获得注塑速度、模具温度和熔体温度对不同厚度制品充填性能的影响,并对成型过程中出现的流动不平衡现象及前沿面形状变化的机理进行了分析.结果表明,型腔充填率随着注塑速度、模具温度、熔体温度的升高而增大,且随着型腔厚度减小,制品实现完整充填越来越困难,工艺操作窗口变窄且注塑速度和模具温度都维持在高水平状态.
参考文献
| [1] | S. Y. Yang;S. C. Nian;S. T. Huang;Y. J. Weng .A study on the micro-injection molding of multi-cavity ultra-thin parts[J].Polymers for advanced technologies,2011(6):891-902. |
| [2] | Sun Kyoung Kim;Sung-Ju Choi;Kwan-Hee Lee .Observation of Instabilities in Flow Front During Micro Injection Molding Process[J].Polymer engineering and science,2010(7):1377-1381. |
| [3] | 姜开宇,横井秀俊.注射成型过程熔体前沿充填不平衡现象的试验研究[J].机械工程学报,2009(02):294-300. |
| [4] | Yao DG.;Kim B. .Simulation of the filling process in micro channels for polymeric materials[J].Journal of Micromechanics and Microengineering,2002(5):604-610. |
| [5] | Lixia Wang;Qian Li;Wenna Zhu;Changyu Shen .Scale effect on filling stage in micro-injection molding for thin slit cavities[J].Microsystem technologies,2012(12):2085-2091. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%