研究变形量、退火温度及稀土Re元素对单晶高温合金再结晶行为的影响.结果表明:随变形量的增加,再结晶区域的面积和深度增加；低变形量下再结晶晶粒数量较少,高变形量下再结晶晶粒数量较多.退火温度影响γ '相溶解率,进而影响再结晶晶粒和晶界形貌,1270℃退火,再结晶晶粒呈枝晶状,晶界有少量M6C碳化物析出；1305℃退火,再结晶晶粒为等轴状,晶界上析出的碳化物尺寸较大、数量较多.随着Re含量的增加,合金的再结晶面积明显减小,Re元素具有抑制再结晶行为的作用.
参考文献
| [1] | 陈荣章.单晶高温合金发展现状[J].材料工程,1995(08):3. |
| [2] | 陶春虎,张卫方,李运菊,施惠基.定向凝固和单晶高温合金的再结晶[J].失效分析与预防,2006(04):1-9. |
| [3] | Li Wang;Florian Pyczak;Jian Zhang;Robert F. Singer .On the role of eutectics during recrystallization in a single crystal nickel-base superalloy - CMSX-4[J].International Journal of Materials Research,2009(8):1046-1051. |
| [4] | D. C. Cox;B. Roebuck;C. M. F. Rae .Recrystallisation of single crystal superalloy CMSX-4[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(4):440-446. |
| [5] | Xie G;Wang L;Zhang J.High temperature creep of directionally solidified Ni base superalloys containing local recrystallization[A].Pennsylvania:Warrendale,TMS,2008:453-460. |
| [6] | 陶春虎;张卫方;施惠基.定向凝固高温合金的再结晶[M].北京:国防工业出版社,2007 |
| [7] | 毛卫民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994 |
| [8] | 胡赓祥;蔡珣.材料科学基础[M].上海:上海交通大学出版社,2006 |
| [9] | 熊继春,李嘉荣,赵金乾,刘世忠,董建新.单晶高温合金DD6再结晶晶界析出相特征及其形成机制[J].金属学报,2009(10):1232-1236. |
| [10] | Bond S D;Martin J W .Surface recrystallization in a single crystal nickel-based supperalloy[J].Journal of Materials Science,1984,19(12):3867-3872. |
| [11] | Blavette D;Caron P;Khan T.An atom-probe study of some fine-scale microstructural features in Ni-based single crystal superalloys[A].New York:TMS,1988:305-314. |
| [12] | C.-Y. Jo;H.-Y. Cho;H.-M. Kim .Effect of recrystallisation on microstructural evolution and mechanical properties of single crystal nickel base superalloy CMSX-2 Part 1-Microstructural evolution during recrystallisation of single crystal[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(12):1665-1670. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%