以硅溶胶和TiCl3水溶液为原料,采用水热合成方法制备了结晶度和长程有序性较高的中孔Ti-MCM-41分子筛.钛的加入提高了中孔分子筛的长程有序性.辅助模板剂的选择对分子筛的合成很重要,其中以四甲基氢氧化铵和四乙基氢氧化铵作辅助模板剂的效果较好.四甲基氢氧化铵的用量对分子筛的结晶度和长程有序性也有影响,用量过高和过低都会降低分子筛的结晶度.合成的分子筛中的钛含量(摩尔分数)可以达到3.75%,进一步增加钛的含量,将不能合成得到中孔结构的分子筛.
参考文献
| [1] | Corma A;Navarro M T;Perez-Pariente J.[J].Journal of the Chemical Society,Chemical Communications,1994(02):147. |
| [2] | Notari B .[J].Catalysis Today,1993,18(02):163. |
| [3] | Clerici M G .[J].Applied Catalysis,1991,68(1-2):249. |
| [4] | Ramaswamy A V;Sivasanker S .[J].Catalysis Letters,1993,22(03):239. |
| [5] | Arends I W C E;Sheldon R A;Wallau M et al.[J].Angewandte Chemie International Edition,1997,36(11):1144. |
| [6] | Beck J S;Vartuli J C;Roth W J et al.[J].Journal of the American Chemical Society,1992,114(27):10834. |
| [7] | Kresge C T;Leonowicz M E;Roth W J et al.[P].USP 5 250 282,1993. |
| [8] | Huo Q;Margolese D I;Ciesla U et al.[J].Nature,1994,368(6469):317. |
| [9] | Pinnavaia T J;Tanev P T;Wang J et al.[J].Materials Research Society Symposium Proceedings,1995,371:53. |
| [10] | Corma A;Camblor MA;Esteve P et al.[J].Journal of Catalysis,1994,145(01):151. |
| [11] | Gontier S;Tuel A .[J].Zeolites,1995,15(07):601. |
| [12] | Koyano K A;Tatsumi T.[J].Chemical Communications,1996(02):145. |
| [13] | Zhang W;Pinnavaia TJ .[J].Catalysis Letters,1996,38(34):261. |
| [14] | Bagshaw SA;Prouzet E;Pinnavaia TJ .TEMPLATING OF MESOPOROUS MOLECULAR SIEVES BY NONIONIC POLYETHYLENE OXIDE SURFACTANTS[J].Science,1995(5228):1242-1244. |
| [15] | Taramasso M;Perego G;Notari B .[P].USP 4 410 501,1983. |
| [16] | Kresge C T;Leonowicz M E;Roth W J et al.[J].Nature,1992,359(6397):710. |
| [17] | Alba M D;Luan Z;Klinowski J .[J].Journal of Physical Chemistry,1996,100(06):2178. |
| [18] | Zhang W;Froba M;Wang J et al.[J].Journal of the American Chemical Society,1996,118(38):9164. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%