利用冷压-烧结技术制备了1BaO-10NiO-NiFe2O4复合陶瓷,研究了1BaO-10Ni-NiFe2O4复合陶瓷物相组成和显微结构以及烧结温度对相对密度和导电率的影响.结果表明,1BaO-10NiO-NiFe2O4复合陶瓷烧结样品中主要含有NiO和NiFe2O4两种,BaO与10NiO-NiFe2O4陶瓷组分反应并形成瞬时液相BaFe2O4和Ba2Fe2O5,且Ba2+离子固溶到基体中,促进致密化烧结;随着烧结温度的升高,样品的相对密度无太大变化,均在97%以上.但样品导电率逐渐增大,当烧结温度为1673K时,1BaO-10NiO-NiFe2O4复合陶瓷达到最大电导率21.16S/cm,是烧结温度为1473K时电导率10.17S/cm的2.08倍.
参考文献
| [1] | Pawlek R P.Inert Anodes:An Update[A].USA:TMS,Warreudale PA,2002:449-456. |
| [2] | Weyand J D;DeYoung D H;Ray S P.Inert Anodes for Aluminium Smelting[M].Washington,DC:Alumisum Company of America,1986:1-516. |
| [3] | Pawlek R P.Inert Anodes for The Primary Aluminum Industry:An Update[A].USA:TMS,Warreudale PA,1996:243-248. |
| [4] | LI Jie;LAI Yan-qing;ZHOU Ke-chao;LI Zhi-you;LIU Ye-xiang .Preparation and preliminary testing of cermet inert anode for aluminum electrolysis[J].Transactions of Nonferrous Metals Society of China,2003(3):663-670. |
| [5] | Keniry J .[J].Journal of the Minerals,Metals & Materials Society,2001,53(05):43-47. |
| [6] | Sadoway D R .[J].Journal of the Minerals,Metals & Materials Society,2001,53(05):34-35. |
| [7] | 席锦会,姚广春,刘宜汉,谢英杰.添加TiO2对镍铁尖晶石惰性阳极材料性能的影响[J].功能材料,2006(08):1242-1245. |
| [8] | 席锦会,姚广春,刘宜汉,张晓明.掺杂MnO2对铁酸镍陶瓷惰性阳极性能的影响[J].过程工程学报,2006(03):495-498. |
| [9] | 席锦会,姚广春,刘宜汉,张小明.V2O5对镍铁尖晶石烧结机理及性能的影响[J].硅酸盐学报,2005(06):683-687. |
| [10] | 张剑红,刘宜汉,席锦会,姚广春.掺杂TiO2的镍铁尖晶石的高温导电性[J].材料与冶金学报,2003(04):271-273. |
| [11] | 田忠良,赖延清,段华南,孙小刚,张刚.掺杂SnO2对NiFe2O4陶瓷电导率的影响[J].矿产保护与利用,2004(05):37-40. |
| [12] | Oliveira M;Agathopoulos S;Ferreira J M F.[J].Acta Materialia,2002(50):1441-1451. |
| [13] | 赖延清,张勇,张刚,李劼,贺跃辉,黄伯云,刘业翔.CaO掺杂对10NiO-NiFe2O4复合陶瓷烧结致密化的影响[J].中国有色金属学报,2006(08):1355-1360. |
| [14] | 张刚,李劼,赖延清,孙小刚.烧结气氛对Ni-Fe尖晶石陶瓷致密化和导电性能的研究[J].功能材料,2005(11):1709-1711. |
| [15] | 赖延清,张刚,李劼,刘业翔.金属含量对Cu-Ni-NiFe2O4金属陶瓷导电性能的影响[J].中南大学学报（自然科学版）,2004(06):880-884. |
| [16] | 张雷,周科朝,李志友,张晓泳.气氛对NiFe2O4陶瓷烧结致密化的影响[J].中国有色金属学报,2004(06):1002-1006. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%