为了研究TRIP钢不同变形量后的使用性能,对TRIP690冷轧镀锌板进行了分别为5%、10%、15%、20%的预应变准静态拉伸,研究不同预应变对TRIP钢的力学性能及加工硬化行为的影响,并通过XRD技术测量残留奥氏体的变化规律.结果表明:预应变对TRIP钢的屈服强度、屈强比、平均加工硬化值影响显著,其中屈服强度和屈强比均随预应变量增大而显著增大,抗拉强度和强塑积均小幅增大;同时由于随拉伸预应变量增大,残留奥氏体持续地向马氏体发生渐进式转变,残留奥氏体含量降低,且剩余的残留奥氏体较为稳定难以诱发相变,使得材料的加工硬化能力明显减弱.

In order to study the performances of TRIP steels after different deformation,quasi-static tensile tests of a cold rolled TRIP 690 steel was conducted with pre-strain of 5%,10%,15% and 20%,and the effects of the different pre-strain on the mechanical properties and work hardening behavior of the TRIP steel were investigated.The variation of residual austenite in the steel was observed by XRD.The results show that different pre-strains have a significant effect on yield strength,yield ratio and average hardening value of the TRIP steel,for which the yield strength and yield ratio increase significantly,tensile strength and product of strength and elongation increase slightly with the increasing of pre-strain.Meanwhile,the residual austenite is transformed to martensite continuously and gradually with the increasing of the tensile pre-strain,and the remained residual austenite is more stable and is difficult for the transformation to martensite,and work-hardening ability of the material decrease significantly.

参考文献

[1] 唐荻;米振莉;陈雨来.国外新型汽车用钢的技术要求及研究开发现状[J].钢铁,2005(6):1-5.
[2] 张卿卿;李大永;彭颖红;汪晨.TRIP780高强度钢板动态力学特性的研究[J].塑性工程学报,2009(6):6-10.
[3] 董瑞;赵爱民;丁然;何建国;李振.退火工艺对1200 MPa级TRIP钢的组织和力学性能的影响[J].材料热处理学报,2015(2):125-130.
[4] 惠卫军;李阳;张永健;周超;董瀚.预应变对中碳TRIP钢氢吸附及延迟断裂行为的影响[J].材料热处理学报,2012(6):42-46.
[5] M. De MEYER.The Influence of the Substitution of Si by Al on the Properties ofCold Rolled C-Mn-Si TRIP Steels[J].ISIJ International,19998(8):813-822.
[6] P. J. JACQUES;J. LADRIERE;F. DELANNAY.On the Influence of Interactions between Phases on the Mechanical Stability of Retained Austenite in Transformation-Induced Plasticity Multiphase Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,200111(11):2759-2768.
[7] M.R. Berrahmoune;S. Berveiller;K. Inal.Analysis of the martensitic transformation at various scales in TRIP steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20041/2(1/2):304-307.
[8] 吴其浩;熊杰;朱娜琼;何燕霖;李麟.高强度TRIP钢中残留奥氏体稳定性[J].材料热处理学报,2013(11):89-92.
[9] 焦多田;蔡庆伍;武会宾.轧后冷却制度对X80级抗大变形管线钢组织和屈强比的影响[J].金属学报,2009(9):1111-1116.
[10] Chiang, J.;Lawrence, B.;Boyd, J.D.;Pilkey, A.K..Effect of microstructure on retained austenite stability and work hardening of TRIP steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201113/14(13/14):4516-4521.
[11] Jie Shi;Xinjun Sun;Maoqiu Wang;Weijun Hui;Han Dong;Wenquan Cao.Enhanced work-hardening behavior and mechanical properties in ultrafine-grained steels with large-fractioned metastable austenite[J].Scripta materialia,20108(8):815-818.
[12] 蔡志辉;辛啟斌;孔辉;丁桦.Fe-11Mn-4Al-0.2C钢的应变硬化行为[J].东北大学学报(自然科学版),2013(12):1721-1724,1729.
[13] 熊自柳;江海涛;蔡庆伍;唐荻;刘仁东.消除TRIP钢屈服平台的预拉伸实验及微观机理[J].北京科技大学学报,2008(4):379-382.
[14] 余海燕 .复杂应变状态下TRIP钢相变诱发塑性行为及其在车身覆盖件中的应用研究[D].上海交通大学,2005.
[15] 定巍;龚志华;唐荻;江海涛;王宝峰.低硅含铝TRIP钢残余奥氏体变形过程中稳定性研究[J].材料工程,2013(12):68-73.
[16] I.B. Timokhina;P.D. Hodgson;E.V. Pereloma.Effect of Microstructure on the Stability of Retained Austenite in Transformation-Induced-Plasticity Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,20048(8):2331-2341.
[17] Seawoong Lee;Seok-Jae Lee;Bruno C. De Cooman.Work hardening behavior of ultrafine-grained Mn transformation-induced plasticity steel[J].Acta materialia,201120(20):7546-7553.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%