利用超低碳和微合金化的成分设计，采用TMCP工艺，充分利用晶粒细化和针状铁素体与粒状贝氏体组织强化、下线堆垛缓冷24h等手段，保证热轧状态达到该钢种需要的屈服强度、伸长率，进而去掉热处理调质及回火工艺，同样在工业试制条件下得到韧性良好、屈服强度为570 M Pa级的超低碳贝氏体钢。
The hot-rolled plate met the requirememt of yield strength and elongation by ultra-low carbon ,micro-allo-ying ,TMCP (Thermomechanical Controlled Proces) ,and offline stackingslow cooling of 24 hours without quench-ing and tempering ,making full use of grain refinement and acicular ferrite and granular bainite strengthening .The ultralow-carbon bainitic steel with good toughness and yield strength of 570MPa grade was produced under the same conditions in the industrial production .
参考文献
| [1] | 夏政海,曹志强,罗登,张永东,卢伟煜,吴开明.超低碳高强度Q550D贝氏体钢的研制[J].钢铁研究学报,2010(06):40-44. |
| [2] | 冯路路.采用TMCP工艺开发低成本高强钢Q550[J].宽厚板,2011(01):30-32. |
| [3] | 赵显鹏,郭怀兵,刘继红,郭伟.Q550D高强钢冲击性能不稳定成因研究[J].轧钢,2010(02):18-19. |
| [4] | 段双霞.低合金高强钢Q550D延伸不合格原因分析[J].山西冶金,2010(01):12-14. |
| [5] | 魏士政,赵德文,蔡晓辉,龚彩军,王君,刘相华,王国栋.控制冷却技术在实际生产中的应用[J].钢铁,2003(09):46-50. |
| [6] | James F. Evans;Michael T. Clark .Plate cooling - technologies and market requirements[J].Iron & Steel Review,2002(6):49-53. |
| [7] | 吕斌,宋波.临钢炼钢工序Q550D成分调整与工艺控制[J].山西冶金,2010(02):38-39,71. |
| [8] | 陈颜堂,郭爱民,贺信莱,付俊岩.回火对铌微合金化C-Mn钢的组织及性能影响[J].金属热处理,2007(06):27-29. |
| [9] | 李凡,衣海龙,陈军平,刘振宇,王国栋.超快冷技术在鞍钢Q55o工程机械用钢生产中的应用[J].轧钢,2011(05):7-8,50. |
| [10] | 崔忠圻;覃耀春.金属学与热处理[M].北京:机械工业出版社,2007 |
| [11] | 王建泽,康永林,杨善武,周建.回火温度对超低碳贝氏体钢（ULCB）组织与性能的影响[J].金属热处理,2007(11):19-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%