为了改善X70管线钢焊接接头慢拉伸电化学腐蚀性能,用激光冲击波对X70管线钢焊接接头表面进行强化处理.采用慢应变速率拉伸法分析了X70管线钢焊接接头,在不同H2S浓度的NACE溶液（0.5%HAC＋5%NaCl）中电化学腐蚀行为,测试了激光冲击处理前后X70管线钢焊接接头腐蚀电位,讨论了激光冲击处理对X70管线钢焊接接头腐蚀电位和断口形貌的影响.实验结果表明,激光冲击处理改善了X70管线钢焊接接头腐蚀性能,其SCC敏感性指数Iscc降低了6%.经激光冲击处理后试样自然腐蚀电位正移,极化电阻逐渐增大,其耐蚀性比原始状态有所提高.
For the improvement of electrochemical corrosion properties of X70 pipeline steel welded joint during slow-strain rate tension,the surface of the welded joint was processed by laser shock wave.The electrochemical corrosion behaviors in NAC solution（0.5%HAC＋5%NaCl） with different H2S concentrations were analyzed,and the corrosion potentials of the welded joint before and after laser shock processing were measured.The effects of laser shock processing on corrosion potentials and fracture morphologies were discussed.The results show that the corrosion resistance is improved by laser shock processing,and the sensitivity index of SCC Iscc decreases about 6%.The spontaneous potential is moved to the positive direction,the polarization resistance is increased gradually,and the corrosion resistance is higher than that in primitive state.
参考文献
| [1] | Zhiyong LIU,Xiaogang LI,Yingrui ZHANG,Cuiwei DU,Guoli ZHAI.Relationship between electrochemical characteristics and SCC of X70 pipeline steel in an acidic soil simulated solution[J].金属学报（英文版）,2009(01):58-64. |
| [2] | C.W.Du,X.G.Li,X.Chen,P.Liang,H.Guo.CREVICE CORROSION BEHAVIOR OF X70 STEEL IN HCO3- SOLUTION UNDER CATHODIC POLARIZATION[J].金属学报（英文版）,2008(04):235-244. |
| [3] | Z.Y. Liu;X.G. Li;C.W. Du;Y.F. Cheng;G;Li;C;W;Du;G;L;Zhai;Y;F;Cheng .Stress Corrosion Cracking Behavior Of X70 Pipe Steel In An Acidic Soil Environment[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(8):2251-2257. |
| [4] | Liu, Z.Y.;Li, X.G.;Cheng, Y.F. .In-situ characterization of the electrochemistry of grain and grain boundary of an X70 steel in a near-neutral pH solution[J].Electrochemistry communications,2010(7):936-938. |
| [5] | 李东,陈怀宁,徐宏.表面纳米化对SS400钢焊接接头应力腐蚀性能的影响[J].焊接学报,2009(03):65-68. |
| [6] | 林健,赵海燕,蔡志鹏,鹿安理,武安娜,鄢东洋.磁处理改善低碳钢焊接接头的耐腐蚀性能[J].焊接学报,2006(01):61-64,68. |
| [7] | 王快社,王文,郭韡,张小龙,尹娟,王文礼.搅拌摩擦焊与手工电弧焊接头电化学腐蚀性能研究[J].稀有金属材料与工程,2010(04):747-749. |
| [8] | 陈旭,李晓刚,杜翠薇,梁平.阴极极化条件下X70钢的缝隙腐蚀行为[J].金属学报,2008(12):1431-1438. |
| [9] | 孔德军,周朝政,吴永忠.304不锈钢激光冲击处理后的残余应力产生机理[J].红外与激光工程,2010(04):736-740. |
| [10] | 邹世坤,王健,王华明.激光冲击处理对焊接接头力学性能的影响（Ⅰ）[J].焊接学报,2001(03):79-81. |
| [11] | 宋颖刚,高玉魁,陆峰,赵振业.TC21钛合金喷丸强化层微观组织结构及性能变化[J].航空材料学报,2010(02):40-44. |
| [12] | 叶雄林,朱有利.超声冲击细化22SiMn2TiB超高强钢焊接接头晶粒研究[J].热加工工艺,2006(23):12-14. |
| [13] | 毕凤琴,张旭昀,王勇,孙丽丽,汪洋.X70管线钢在湿H2S环境中的应力腐蚀行为研究[J].材料工程,2009(08):15-18,23. |
| [14] | 张亮,李晓刚,杜翠薇,刘智勇,梁平.X70管线钢在含CO2库尔勒土壤模拟溶液中的腐蚀行为[J].金属学报,2008(12):1439-1444. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%